搪瓷用钢抗鳞爆性能的研究现状

发布时间：2018-05-20 12:31

  本文选题：搪瓷用钢 + 鳞爆　； 参考：《表面技术》2016年12期

【摘要】：介绍了鳞爆形成机理,分析了材料成分和加工工艺2个主要因素对析出相种类及数量、晶粒级别和抗鳞爆性能的影响。通过改善搪瓷用钢的组成成分、制定合理的轧制和退火工艺等措施来增加钢中不可逆陷阱数量,可以提高钢的贮氢性能,减少鳞爆的发生。并对国内外抗鳞爆性能评价技术的发展现状以及最常用的评价抗鳞爆性能的方法进行了相关介绍。
[Abstract]:The formation mechanism of scale explosion was introduced and the effects of material composition and processing technology on the type and quantity of precipitated phase grain grade and scale explosion resistance were analyzed. By improving the composition of enamel steel and making reasonable rolling and annealing process to increase the number of irreversible traps in steel, the hydrogen storage performance of steel can be improved and the occurrence of scale explosion can be reduced. The development status of scale explosion resistance evaluation technology at home and abroad and the most commonly used methods to evaluate scale explosion resistance are also introduced.
【作者单位】： 上海应用技术大学机械学院;
【分类号】：TG142.1;TG335.5;TG156.2

【相似文献】

相关期刊论文 前10条

1 孙全社,陆匠心,金蕾,张庆安,袁晓敏;加钛超低碳钢成形性能和贮氢性能的研究[J];钢铁;2000年01期

2 张金龙;林根文;方守狮;李晓春;葛建生;;钛钒铬基合金的贮氢性能研究[J];上海金属;2006年03期

3 李晓杰;孙智;徐春;;钒钛微合金搪瓷钢中析出相和贮氢性能的研究[J];热处理;2013年04期

4 王启东,吴京,张连瑛,陈长聘;加入铈混合稀土和镍改善镁基合金贮氢性能的研究[J];稀有金属;1984年01期

5 杨丽颖;董小平;耿晓光;王青;林玉芳;张羊换;;稀土镁镍系合金的循环贮氢性能与粉化特性研究[J];粉末冶金工业;2011年02期

6 王同涛;王树茂;黄卓;蒋利军;刘晓鹏;;钛催化氢化铝钠的贮氢性能[J];中国有色金属学报;2006年08期

7 李晋平;徐文e，

本文编号：1914633