回火温度对高碳钢断裂韧性的影响

发布时间：2018-06-01 23:52

  本文选题：回火温度 + 高碳钢　； 参考：《钢铁研究学报》2017年06期

【摘要】：研究了回火温度对高碳钢断裂韧性及其他力学性能的影响。利用紧凑拉伸试样测量其平面应变断裂韧度,扫描电镜(SEM)观察回火后的组织演变规律及断裂韧度试样断口形貌。结果表明:随着回火温度的升高,马氏体逐渐分解消失,从过饱和α固溶体中析出的碳化物数量逐渐增多并发生聚集长大,强度和硬度下降,塑性、断裂韧性和冲击韧性上升。位错强化和固溶强化作用减弱是试验钢强度降低、韧性升高的主要原因。
[Abstract]:The effect of tempering temperature on fracture toughness and other mechanical properties of high carbon steel was studied. The plane strain fracture toughness of compact tensile specimens was measured and the microstructure evolution and fracture morphology of tempered specimens were observed by SEM (SEM). The results show that with the increase of tempering temperature, martensite gradually decomposes and disappears, and the amount of carbide precipitated from supersaturated 伪 solid solution increases and accumulates and grows, the strength and hardness decrease, and the plasticity, fracture toughness and impact toughness increase. Dislocation strengthening and solution strengthening are the main reasons for the decrease of test steel strength and the increase of toughness.
【作者单位】： 钢铁研究总院特殊钢研究所;晋西工业集团有限责任公司;
【基金】：国家自然科学基金青年基金资助项目(51301042)
【分类号】：TG142.1;TG161

【相似文献】

相关期刊论文 前10条

1 曹士暖;;确定碳素钢回火温度的经验公式[J];金属热处理;1960年03期

2 栗世奇;;一些常用钢的回火温度表[J];机械工人技术资料;1973年04期

3 宋延沛,祝要民,朱景芝;回火温度对高碳中锰钢性能的影响[J];热加工工艺;2000年06期

4 贺秀丽;关小军;徐洪庆;王连杰;李国保;;回火温度对高强度容器钢组织结构与性能的影响[J];山东轻工业学院学报(自然科学版);2007年03期

5 李继红;李岩;张海存;支金花;张敏;;回火温度对40CrNiMo7钢组织与性能的影响[J];金属热处理;2011年07期

6 王良;;几种常用钢回火温度的确定[J];机械工人;1958年04期

7 王良;;几种常用掽回火温度的确定[J];机械工人;1958年05期

8 任恒山;;降低回火温度提高煤水幨，

本文编号：1966282