回火温度对W6Mo5Cr4V2高速钢深冷处理后性能的影响

发布时间：2018-06-10 13:04

  本文选题：高速钢 + 深冷处理　； 参考：《金属热处理》2017年01期

【摘要】：测试了W6Mo5Cr4V2高速钢深冷处理后的残余应力、硬度和抗弯强度随回火温度的变化。结果表明:深冷处理后,随着回火温度的升高,残余压应力减小,440℃时应力最小,之后有小幅回升;随回火温度的升高会出现二次硬化现象,硬度值在440℃时取得极大值,之后反向;抗弯强度值在回火温度较低时变化率较小,回火温度较高时,抗弯强度随回火温度的升高显著增加。随着回火温度的升高,W6高速钢的性能逐渐改善,回火温度在440~560℃之间时,W6高速钢残余应力和硬度的性能较优,考虑到抗弯强度的影响,在此温度区间回火温度越高,综合力学性能越好。
[Abstract]:The residual stress, hardness and bending strength of W6Mo5Cr4V2 high speed steel after cryogenic treatment were tested with the change of tempering temperature. The results showed that the residual compressive stress decreased with the increase of tempering temperature and the minimum stress at 440 C after cryogenic treatment, and then a small amplitude, and two hardening phenomena with the increase of tempering temperature and the hardness value of 440 degrees C. When the tempering temperature is high, the flexural strength increases significantly with the tempering temperature. As the tempering temperature increases, the performance of the W6 high speed steel is improved gradually. The performance of the residual stress and hardness of the W6 high speed steel is better than the tempering temperature of 440~560. Excellent, considering the effect of bending strength, the higher tempering temperature in this temperature range, the better comprehensive mechanical properties.
【作者单位】： 太原科技大学机械工程学院;
【基金】：国家自然科学基金(51275333)
【分类号】：TG142.1;TG161

【相似文献】

相关期刊论文 前10条

1 曹士暖;;确定碳素钢回火温度的经验公式[J];金属热处理;1960年03期

2 栗世奇;;一些常用钢的回火温度表[J];机械工人技术资料;1973年04期

3 宋延沛,祝要民,朱景芝;回火温度对高碳中锰钢性能的影响[J];热加工工艺;2000年06期

4 贺秀丽;关小军;徐洪庆;王连杰;李国保;;回火温度对高强度容器钢组织结构与性能的影响[J];山东轻工业学院学报(自然科学版);2007年03期

5 李继红;李岩;张海存;支金花;张敏;;回火温度对40CrNiMo7钢组织与性能的影响[J];金属热处理;2011年07期

6 王良;;几种常用钢回火温度的确定[J];机械工人;1958年04期

7 王良;;几种常用掽回火温度的确定[J];机械工人;1958年05期

8 任恒山;;降低回火温度提高煤水幨，

本文编号：2003319