固溶处理对热压CoCrW合金组织及力学性能的影响

发布时间：2018-08-07 19:26

【摘要】：利用SEM,XRD和TEM等分析手段研究了固溶处理对热压烧结CoCrW合金相组成的影响,通过硬度测试、室温拉伸和摩擦磨损实验,研究了固溶处理对热压烧结CoCr W合金力学性能的影响.结果表明,热压态与固溶态CoCrW合金的组成相均为M_(23)C_6,M_6C,CrCo金属间化合物和γ-Co基体;固溶处理降低了合金中的M_(23)C_6含量和原始颗粒边界数量,同时改善了合金塑性和耐磨性能.合金室温硬度和抗拉强度均随固溶温度升高、固溶时间延长而先增高后降低.
[Abstract]:The effect of solution treatment on the phase composition of hot press sintered CoCrW alloy was studied by means of TEM and TEM. The effect of solution treatment on mechanical properties of hot-pressed CoCr W alloy was studied by hardness test, tensile test at room temperature and friction and wear test. The results show that the composition phases of hot pressed and solid solution CoCrW alloys are M23 C _ (23) C _ (6) C _ (6) C _ (6) C _ (6) CrCo intermetallic compound and 纬 -Co matrix, the content of M23 C _ (6) C _ (6) and the number of original particle boundaries in the alloy are decreased by solution treatment, and the plasticity and wear resistance of the alloy are improved. The hardness and tensile strength of the alloy increase with the increase of the solution temperature and the solution time increases first and then decreases.
【作者单位】： 太原科技大学材料科学与工程学院;驻某厂军代表室;中国科学院金属研究所;
【基金】：国家自然科学基金资助项目51201161~~
【分类号】：TG166.7;TG146.16

【相似文献】

相关期刊论文 前10条

1 钱佳;朱丽娟;刘瑞华;刘越;;Mg-6Al-0.5Y-1.0Ce合金固溶处理工艺的研究[J];热加工工艺;2009年04期

2 朱冉冉;张永安;熊柏青;李志辉;李锡武;刘红伟;朱宝宏;王锋;;单级固溶处理对7136铝合金组织及力学性能的影响[J];航空材料学报;2012年05期

3 刘诚毅;杨政民;;1Cr18Ni9Ti固溶处理工艺对机械性能的影响[J];航空精密制造技术;1990年04期

4 黄世民;铝合金挤压制品固溶处理不均匀性的研究[J];航空工艺技术;1992年02期

5 吴鹤,韩雅芳,陈熙琛,周彦邦;固溶处理对钛硅共晶合金组织与断裂行为的影响[J];铸造;2002年05期

6 郝广瑞,王洪斌,黄进峰,杨滨,张永安,熊柏青,张济山;喷射成形超高强度Al-Zn-Mg-Cu合金的固溶处理[J];北京科技大学学报;2004年05期

7 蒋寿生;宁爱林;肖似蹼;;高强铝合金快速固溶工艺研究[J];邵阳学院学报(自然科学版);2005年04期

8 黄振宝;张新明;刘胜胆;刘文辉;张，

本文编号：2171110