铈元素对H13模具钢等向性能影响的研究

发布时间：2018-08-15 18:23

【摘要】：对H13热作模具钢进行了Ce元素处理,配合等温球化热处理工艺,开展了对H13钢等向性能的研究。采用JBN-300摆锤式冲击试验机对冲击韧性进行了检测,采用MICROHARDNESS TESTER HV-1000显微硬度仪对显微硬度进行了检测。结果表明:随Ce含量的增加,H13钢的横、纵向力学性能呈先增加后减小的趋势,当Ce含量为0.05%时钢的等向性能有大幅提高且达到最大值91.10%;Ce元素对显微硬度影响不大;添加Ce元素钢的等向性能都有不同程度的增加。
[Abstract]:The isotropic properties of H13 steel were studied by means of ce element treatment and isothermal spheroidizing heat treatment. Impact toughness was tested by JBN-300 pendulum impact tester and microhardness was tested by MICROHARDNESS TESTER HV-1000 microhardness tester. The results show that the transverse and longitudinal mechanical properties of H13 steel increase firstly and then decrease with the increase of ce content. When the ce content is 0.05, the isotropic properties of the steel increase greatly and the maximum value of 91.1010Ce has little effect on the microhardness. The isotropic properties of ce steel were increased to some extent.
【作者单位】： 贵州大学材料与冶金学院;贵州省冶金工程与过程节能重点实验室;
【基金】：贵州省科技厅重点工业攻关项目(黔科合GY[2012]3016)资助
【分类号】：TG142.1

【相似文献】

相关期刊论文 前10条

1 顾佳羽;李欢;;高温正火对H13钢锻后组织的影响[J];金属热处理;2012年06期

2 蒋留全,楼培炯,王逸民,张培林,华勤;无醇溶剂陶瓷型工艺浇铸H13钢模具[J];特种铸造及有色合金;1993年05期

3 任慧平,李文学,刘宗昌,戴建明,孙久红,顾容;碳化物对H13钢退火软化的影响[J];钢铁研究学报;1997年05期

4 胡活;张燕;韩济才;;H13钢锻模型腔超塑成形工艺研究(续)[J];金属成形工艺;1994年06期

5 陈希春,徐卫国,周德光,傅杰;感应电渣离心浇铸生产H13钢斜轧辊毛坯的质量分析[J];特殊钢;2001年03期

6 任慧平，李文学，刘宗昌，王玉峰;H13钢软化退火工艺的研究[J];热加工工艺;1996年06期

7 陈玉华;吴晓春;汪宏斌;;喷丸对H13钢等离子渗氮处理的影响[J];金属热处理;2008年06期

8 邱建明;史厚忠;;H13钢铝合金压铸模的失效分析[J];金属热处理;2011年04期

9 张金祥;卢林;王和斌;黄进峰;崔华;张济山;;喷射成形H13钢的微观组织及形成特点[J];材料导报;2014年06期

10 庞祖高;苏广才;林松;刘琼;;H13钢温挤压模具型腔开裂失效分析与控制[J];模具工业;2008年11期

相关会议论文 前3条

1 吴晓春;闵娜;陈玉华;汪宏斌;;喷丸对H13钢热疲劳性能的影响[A];第七届全国表面工程学术会议暨第二届表面工程青年学术论坛论文集（一）[C];2008年

2 张德美;叶建平;李晓东;;模具H13钢淬火后裂纹产生原因分析[A];2007年全国失效分析学术会议论文集[C];2007年

3 张德美;叶建平;李晓东;;H13钢制成的模具淬火后裂纹产生原因分析[A];2007年中国机械工程学会年会论文集[C];2007年

相关硕士学位论文 前3条

1 周莹;形状耦元与热疲劳温度对H13钢热疲劳性能的影响[D];吉林大学;2014年

2 尹德猛;脉冲电流处理H13钢组织演变及热疲劳行为的研究[D];吉林大学;2010年

3 冯新;基于电火花加工方法的H13钢表面强化研究[D];大连理工大学;2007年

，

本文编号：2185028