复合添加Cr、Mn、Ti对7136铝合金组织及力学性能的影响

发布时间：2018-09-03 15:43

【摘要】：采用井式坩埚炉熔炼铸造了3种铝合金,通过金相分析、硬度测试、力学拉伸、断口扫描研究了过渡族元素对7136铝合金组织和性能的影响。结果表明,过渡族元素能够细化铸态组织,复合添加Cr、Mn、Ti后晶粒细化效果明显,能够抑制铝合金板材再结晶,提高抗拉强度,使伸长率提高15%,改变了断裂方式,提高了综合力学性能。
[Abstract]:Three kinds of aluminum alloys were cast in a well crucible furnace. The effect of transition elements on the microstructure and properties of 7136 aluminum alloy was studied by metallographic analysis, hardness test, mechanical tensile test and fracture scanning. The results show that the transition elements can refine the as-cast structure, and the effect of grain refinement is obvious after the addition of Cr,Mn,Ti, which can inhibit the recrystallization of aluminum alloy plate, improve the tensile strength, increase the elongation by 15%, and change the fracture mode. The comprehensive mechanical properties are improved.
【作者单位】： 烟台南山学院工学院材料系;中南大学材料科学与工程学院;
【分类号】：TG146.21

【相似文献】

相关期刊论文 前7条

1 刘玉梅,李吉学,刘宏建,苏文辉;少量元素掺杂对Y-Ba-Cu-O强化的影响[J];吉林大学自然科学学报;1989年01期

2 杨恩波;;离子交换色谱法分离铀同位素[J];中国原子能科学研究院年报;1986年00期

3 李东;刘羽寅;;钛合金热稳定性研究 Ⅱ.过渡族元素在Ti_3X相形成中的行为[J];金属学报;1984年06期

4 王永海;梁忠华;毛翔;;7022-T6、T73和T76热处理状态的电镜观察[J];轻合金加工技术;1993年06期

5 崔玉友,李东,万晓景;Ti合金中ω相的形成规律[J];金属学报;1993年02期

6 张彦生;γ-Fe-Mn-Al-Cr-Si系合金Néel温度与合金成分的关系[J];材料科学进展;1988年02期

7 ;[J];;年期

相关会议论文 前1条

1 朱祥坤;郭跃玲;何学贤;杨淳;张巧大;;过渡族元素同位素分异理论体系及其在全球环境变化研究中的应用[A];“十五”重要地质科技成果暨重大找矿成果交流会材料四——“十五”地质行业重要地质科技成果资料汇编[C];2006年

相关硕士学位论文 前1条

1 张宇;过渡族元素添加对CuZr基金属玻璃耐蚀性的影响[D];东北大学;2011年

，

本文编号：2220426