TC27钛合金疲劳断裂特性研究
发布时间：2018-09-14 11:39
【摘要】：钛合金是航空领域应用十分广泛的金属材料之一。通过进行断裂韧度测试试验和腐蚀环境下的裂纹扩展速率试验,研究了TC27钛合金疲劳断裂特性,将TC27钛合金的疲劳断裂特性与Ti55531钛合金进行了对比。结果表明:TC27与Ti55531的疲劳性能基本持平。
[Abstract]:Titanium alloy is one of the widely used metal materials in aviation field. The fatigue fracture characteristics of TC27 titanium alloy were studied by means of fracture toughness test and crack growth rate test under corrosion environment. The fatigue fracture characteristics of TC27 titanium alloy were compared with that of Ti55531 titanium alloy. The results show that the fatigue properties of TC27 and Ti55531 are basically equal.
【作者单位】： 中航工业成都飞机工业(集团)有限责任公司技术中心;西北工业大学力学与土木建筑学院;
【基金】：国家自然科学基金项目(5140539)
【分类号】：TG146.23
[Abstract]:Titanium alloy is one of the widely used metal materials in aviation field. The fatigue fracture characteristics of TC27 titanium alloy were studied by means of fracture toughness test and crack growth rate test under corrosion environment. The fatigue fracture characteristics of TC27 titanium alloy were compared with that of Ti55531 titanium alloy. The results show that the fatigue properties of TC27 and Ti55531 are basically equal.
【作者单位】： 中航工业成都飞机工业(集团)有限责任公司技术中心;西北工业大学力学与土木建筑学院;
【基金】：国家自然科学基金项目(5140539)
【分类号】：TG146.23
【相似文献】
相关期刊论文 前10条
1 张振芳,张天宜,刘民治;中碳铬镍钼钢的断口特征值与断裂韧度之间的关系[J];金属学报;1981年03期
2 魏嘉荃 ,钟伯明 ,李其;低温下利用J—R曲线确定延性断裂韧度丁J_(1c)的研究[J];大庆石油学院学报;1984年02期
3 张永信;兵器用高强钢延性断裂韧度的试验确定[J];兵器材料科学与工程;1991年09期
4 洪永先;;高强度变形铝合金断裂韧度的改进[J];轻金属;1979年05期
5 郑秀瑗;;低温断裂韧度的测试技术[J];试验机与材料试验;1981年03期
6 周公良,何耀祖;铝、钛合金平面应变断裂韧度判据的研究[J];稀有金属;1982年02期
7 雷斌隆;用边缺口小试样评定母材及焊接接头断裂韧度的研究[J];压力容器;1984年04期
8 俞灌兴;利用阻力曲线测定金属材料的动态断裂韧度K_(1d)[J];南昌大学学报(理科版);1987年02期
9 张利民,谢华;卸载柔度法测材料的断裂韧度J_(1c)[J];试验技术与试验机;1992年05期
10 李焕喜,陈昌麒;高强度变形铝合金断裂韧度各向异性的机理和预测[J];金属学报;1992年03期
相关会议论文 前7条
1 邱保文;李荣锋;Q糜，
本文编号：2242606
本文链接：https://www.wllwen.com/kejilunwen/jiagonggongyi/2242606.html