Achieving higher strength in Cu–Ag–Zr alloy by warm/hot roll

发布时间：2021-05-23 01:06

　　High-strength Cu–3Ag–0.5Zr alloy plates were produced by multi-pass rolling in the temperature range of500–800 °C. An increase in strength was observed by rolling in the aforementioned range without significant loss in ductility. All the rolled samples show higher strength than solution-treated and aged samples. The maximum strength was observed for plates rolled at 500 °C with a yield strength and ultimate tensile strength of 311 and385 MPa, respectively, and retaining a ductility of 23 %.Trans... 