Effect of Al22Si/ZL102 bimetal interface fabricated by extru

发布时间：2022-10-10 14:07

　　The Al22Si/ZL102 bimetal was designed and prepared by extrusion at near-eutectic temperature.The properties and fracture behaviors of different surface treatments between oxide film and zinc coating were compared between the Al22 Si and ZL102 bimetal.The average bonding strength of bimetal with intermittent oxide film interface was about 89.3MPa,which is higher than that of the bimetal fabricated by zinc coating method（about 76.3MPa）.During the process of extrusion,the oxidation film was extrude... 

【文章页数】：6 页