抗车辙柔性基层沥青混合料的力学性能

发布时间：2018-05-02 12:18

  本文选题：抗车辙 + 柔性基层　； 参考：《材料科学与工程学报》2014年05期

【摘要】：优选三种沥青,两种抗车辙级配,通过大量室内试验,铺筑试验路和试验路跟踪观测,研究了抗车辙柔性基层沥青混合料的力学性能。结果表明:与半刚性基层相比,抗车辙柔性基层混合料劈裂模量很低,具有良好的抗变形能力,抗压和劈裂强度大,抗压回弹模量不比半刚性基层材料低,在保证其下卧层有足够强度和刚度的条件下,能够用于重载交通沥青路面。
[Abstract]:Three kinds of asphalt and two kinds of anti-rutting gradation were selected. The mechanical properties of asphalt mixture with rut-resistant flexible base were studied through a large number of indoor tests and tracing observation of paving test road and test road. The results show that, compared with semi-rigid base, the anti-rutting flexible base mixture has low splitting modulus, good deformation resistance, high compressive and splitting strength, and no lower modulus of compressive resilience than semi-rigid base material. It can be used in heavy duty traffic asphalt pavement under the condition of sufficient strength and rigidity.
【作者单位】： 湖南科技学院;重庆交通大学;
【基金】：湖南省教育厅科研资助项目(08C193)
【分类号】：U414

【相似文献】

相关期刊论文 前10条

1 于刚;张高峰;张敬果;;大粒径透水性沥青混合料(LSPM-30)柔性基层施工方法[J];科技致富向导;2010年20期

2 段新迎,杨永生,何荣大;柔性基层在东红路大修工程中的应用[J];路基工程;2005年05期

3 邢小兵;;柔性基层沥青混凝土路面施工质量控制[J];公路交通科技(应用技术版);2006年05期

4 邱志雄;;柔性基层在粤赣高速公路长陡坡沥青路面的应用[J];广东公路交通;2007年02期

5 吕旭溪;;在路面病害治理中柔性基层的应用[J];黑龙江科技信息;2008年05期

6 韩红;;对柔性基层沥青混凝土路面施工的试验研究[J];黑龙江交通科技;2008年02期

7 陈锋锋;黄晓明;单景松;;重载下不同基层沥青路面的力学分析[J];上海公路;2008年02期

8 郑建，

本文编号：1833885