连续球压痕法测试压力容器钢力学性能的研究

发布时间：2018-01-31 16:13

本文关键词： 力学性能无损测试连续球压痕压力容器钢　出处：《振动.测试与诊断》2015年02期 　论文类型：期刊论文

【摘要】：为探讨材料力学性能无损测试的新方法,分析研究了连续球压痕试验测试材料力学性能的原理,并以压力容器用钢15CrMoR,Q245R,Q345R等3种钢板为研究对象,采用连续球压痕试验与常规拉伸试验相比较的方法,测试了屈服强度、抗拉强度等力学性能,深入开展了连续球压痕试验与常规拉伸试验所测试力学性能的比对分析工作。比对结果表明了连续球压痕试验在测试压力容器用钢力学性能方面的可行性、可靠性与准确性,证明连续球压痕试验法可以应用于工程中部分材料力学性能的无损检测。
[Abstract]:In order to explore a new method for nondestructive testing of mechanical properties of materials, the principle of continuous ball indentation test for testing mechanical properties of materials was analyzed and studied, and the steel 15CrMoR Q245R for pressure vessels was used. The yield strength and tensile strength of Q345R steel plate were tested by comparing continuous ball indentation test with conventional tensile test. The comparison and analysis of mechanical properties between continuous ball indentation test and conventional tensile test are carried out. The results show the feasibility of continuous ball indentation test in testing mechanical properties of pressure vessel steel. It is proved that the continuous ball indentation test method can be applied to the nondestructive testing of mechanical properties of some materials in engineering.
【作者单位】：山东大学机械工程学院;浙江省特种设备检验研究院;山东省特种设备安全工程技术研究中心;山东大学特种设备安全保障与评价研究中心;
【基金】：国家重点基础研究发展计划(“九七三”计划)资助项目(2011CB013401)
【分类号】：TG142.15
【正文快照】： 引言工业生产和设备服役的安全已经被提到了一个前所未有的高度,而事实上,影响工业设备安全评估的材料性能的获得却一直是瓶颈,也是专家学者的研究重点。通常,压力容器用钢加工制造成压力容器设备并服役后,一般只能定期对其进行缺陷检测和日常维护,而由于常规力学性能测试大都

【共引文献】