基于铝镁硅合金电阻计算的MИTИCCEH-ΦИЛEMHГ规则修正

发布时间：2018-02-01 07:03

本文关键词： MИTИCCEH-ΦИЛEMHГ规则修正合金导线电阻率增值变量计算模型误差率优化与预测理论依据　出处：《沈阳工业大学学报》2015年02期 　论文类型：期刊论文

【摘要】：为了解决因缺少对合金元素与电阻之间的定性定量研究所导致的当前生产或实验过程依然以简单的实验法来制备所需导线的问题,基于MИTИCCEH-ΦИЛEMHГ规则对电阻率的定义性描述,引入由合金元素引起的缺陷电阻率增值变量,建立合金元素与电阻率的计算模型.结果表明,在相同工艺条件下,对于不同合金成分Al-Mg-Si合金导线而言,其修正规则计算模型计算值与实测值更为吻合,误差率不大于0.5%.因此,此计算模型可以作为优化和预测合金导线成分设计的理论依据.
[Abstract]:In order to solve the problem that the current production or experimental process caused by the lack of qualitative and quantitative research on alloy elements and resistance is still using simple experimental method to prepare the required conductors. Based on the definitional description of resistivity by EMH rule, the increment variable of defect resistivity caused by alloying elements is introduced. The calculation model of alloy elements and resistivity is established. The results show that under the same process conditions, for Al-Mg-Si alloy wires with different alloy composition. The calculated value of the modified rule model is more consistent with the measured value, and the error rate is not greater than 0.5. Therefore, this model can be used as the theoretical basis for optimizing and predicting the composition design of alloy conductor.
【作者单位】：沈阳工业大学材料科学与工程学院;
【基金】：辽宁省科技攻关计划项目(2013201018)
【分类号】：TG146.21
【正文快照】： 目前,在超高压、高压、中低压设备及线缆的应用中,铝及铝合金以其优异的导电性能及铸造性能得到广泛认同,但由于铝及铝合金强度问题,其应用在某些领域受到限制,如,在远程输电过程中,主要以钢芯铝绞线的形式出现,这不但增加了应用成本,也加大了回收难度.随着“十二五”计划对国

【参考文献】