应力比对K55套管钻井钢疲劳裂纹扩展性能的影响

发布时间：2018-02-20 15:13

  本文关键词： K套管钻井钢 应力比R 疲劳裂纹扩展性能 应力强度因子范围ΔK 断口形貌　出处：《材料工程》2015年06期 　论文类型：期刊论文

【摘要】：利用电液伺服疲劳实验机及SEM研究了应力比对K55套管钻井钢疲劳裂纹扩展行为的影响。结果表明:应力比对裂纹失稳区起始点对应的应力强度因子范围ΔK值具有显著的影响。随着应力比的增加,裂纹扩展失稳区起始点对应的裂纹扩展速率具有显著的降低,疲劳裂纹扩展门槛值也呈现显著的降低趋势。当疲劳裂纹逐渐由Paris区过渡到失稳扩展区,平均载荷逐渐取代应力强度因子幅度ΔK作为裂纹扩展的主导驱动力。当裂纹扩展至拉伸过载区,断口表面则呈现明显的冲击断裂特征。
[Abstract]:The effects of stress ratio on the fatigue crack growth behavior of K55 casing drilling steel have been studied by using electro - hydraulic servo fatigue test machine and SEM . The results show that the stress ratio has a significant influence on the stress intensity factor range . DELTA.K value corresponding to the starting point of crack propagation . As the stress ratio increases , the crack growth rate corresponding to the starting point of crack propagation instability region has a significant decrease . When fatigue crack is gradually transferred from Paris region to unstable expansion region , the average load gradually replaces the stress intensity factor amplitude . DELTA.K as the dominant driving force for crack propagation .

【作者单位】： 西安石油大学材料科学与工程学院;中国石油集团石油管工程技术研究院;
【基金】：青年科技创新基金项目(Z12180) 陕西省重点学科专项资金资助项目(YS32030203) 陕西省教育厅自然科学基金(Z12201)
【分类号】：TG142.1

【共引文献】

相关期刊论文 前1条

1 宋振雷;倪大勇;吴宁祥;谢里阳;;铝合金挤压型材试样加工工艺及疲劳性能研究[J];工程与试验;2015年01期

相关博士学位论文 前1条

1 林杰威;涡扇发动机风扇叶片疲劳寿命评估与可靠性分析[D];天津大学;2013年

相关硕士学位论文 前3条

1 陈咪囡;辙叉用高锰钢疲劳裂纹扩展行为的研究[D];燕山大学;2014年

2 康少憐;变形工艺参数对TA2、TC4钛合金组织性能影响的研究[D];沈阳航空航天大学;2015年

3 阎玫江;φ139.7mm套管循环夹持头关键系统研究[D];北京化工大学;2014年

【二级参考文献】

相关期刊论文 前4条

1 程茜;董建新;张麦仓;;三代粉末高温合金的特征及发展[J];世界钢铁;2011年05期

2 刘永刚;苏建文;林凯;冯耀荣;;一例S135钻杆本体断裂原因分析[J];石油矿场机械;2007年05期

3 王长义;刘正;;压铸态AZ91镁合金疲劳断口组织与裂纹扩展机制[J];特种铸造及有色合金;2008年01期

4 毛萍莉;李扬;刘正;贾莹莹;陈立佳;;挤压态AZ31镁合金的疲劳行为研究[J];特种铸造及有色合金;2010年03期

，

本文编号：1519276