碳钢表面铈盐钝化后的耐腐蚀性能
本文关键词： 铈盐钝化 碳钢 防腐蚀性能 出处：《材料保护》2015年09期 论文类型：期刊论文
【摘要】：以硝酸铈溶液为钝化液,辅以过氧化氢氧化剂,对碳钢进行化学浸泡处理,以达到缓蚀的目的。采用硫酸铜点滴、电化学交流阻抗谱、中性盐雾腐蚀方法,研究了钝化液不同p H值、硝酸铈浓度时的钝化效果。结果表明:以硝酸铈浓度为1 000 mg/L,p H值为2进行钝化,碳钢具有较好的硫酸铜点滴性能、耐中性盐雾腐蚀性能,最大的交流阻抗值,钝化效果最好。
[Abstract]:Using cerium nitrate solution as passivating solution and hydrogen peroxide oxidant, carbon steel was treated by chemical immersion in order to achieve the purpose of corrosion inhibition. Copper sulfate drop, electrochemical impedance spectroscopy and neutral salt spray corrosion method were used. The passivation effect of passivating solution with different pH value and cerium nitrate concentration was studied. The results showed that the carbon steel had good droplet performance of copper sulfate and resistance to neutral salt spray corrosion when the concentration of cerium nitrate was 1 000 mg / L / L H value 2. The maximum AC impedance, passivation effect is the best.
【作者单位】： 武汉大学资源与环境科学学院;中国电力科学研究院;湖北昊为涂料涂装有限公司;
【基金】：国家电网公司科技项目(EPRIGYKJ[2012]8843号)资助
【分类号】：TG174.4
【相似文献】
相关期刊论文 前10条
1 孙桐,周涵新,郭曼丽,张淑焕;纤维素的高分子化学转化及其变性的研究——ⅩⅣ.水-铈盐-丙烯腈-~栁亟泳巯低持械木鄯从推嘟泳鄯╗J];高分子通讯;1964年02期
2 于锦,郭春光,徐炳辉;铈盐对电镀锡参数和性能的影响[J];表面技术;2004年02期
3 陆鑫;郭瑞光;姚倩;乔亚龙;童少磊;刘江涛;;锌件表面铈盐转化及膜层的耐蚀性[J];材料保护;2012年06期
4 吴海江;徐国荣;许剑光;徐红梅;吴玉蓉;颜焕元;;热镀锌钢铈盐/硅烷复合膜的制备及其耐蚀性能[J];材料保护;2013年01期
5 徐斌;满瑞林;倪网东;胡豫;曹晓燕;颜莎;史燕;;镀锌钢板表面硅烷、铈盐复合膜的制备及耐腐蚀性能研究[J];涂料工业;2007年12期
6 王海川,王光信;用铈盐为媒质电合成芳醛的研究进展[J];青岛化工学院学报;1997年02期
7 孔纲;孙子文;吴双;车淳山;宿孝涛;贺光宗;黄永利;;热镀锌层柠檬酸改进型铈盐转化膜工艺[J];电镀与涂饰;2012年08期
8 赵景茂;霍品;赵旭辉;左禹;;脉冲电场下铝阳极氧化膜铈盐封闭的研究[J];腐蚀科学与防护技术;2012年04期
9 李朝阳，，丘坤元;铈盐－过硫酸盐复合引发体系的研究[J];高分子学报;1994年06期
10 王帅星;赵晴;杜楠;邵志松;舒伟发;陈庆龙;;铈盐对铝合金硼酸?硫酸阳极氧化膜的封闭效应[J];中国有色金属学报;2012年04期
相关会议论文 前1条
1 童格后;陆炜忠;高仁孝;邱刚;王克勇;;铈盐快速(1s)XRF痕量分析法初探[A];第9届全国核电子学与核探测技术学术年会论文集[C];1998年
相关硕士学位论文 前2条
1 霍品;脉冲电场作用下铈盐对铝阳极氧化膜的封闭作用[D];北京化工大学;2012年
2 史立平;封闭处理对镀锌钢表面铈盐化学转化膜耐蚀性的影响[D];西安建筑科技大学;2013年
本文编号：1548432
本文链接：https://www.wllwen.com/kejilunwen/jinshugongy/1548432.html