渗碳方式对18CrNi4A钢齿轮渗层的影响

发布时间：2018-03-11 11:01

  本文选题：CrNiA钢齿轮　切入点：渗碳层　出处：《金属热处理》2015年12期 　论文类型：期刊论文

【摘要】：对18CrNi4A钢齿轮试件分别采取可控气氛和低压真空两种方式进行渗碳,研究了渗碳方式对齿轮渗碳层组织的影响。结果表明,在齿高中部有效硬化层深度相近的情况下,与可控气氛渗碳相比,低压真空渗碳处理的齿根圆角处有效硬化层深度显著增加。采取低压真空渗碳处理的齿轮,渗层中碳化物呈细小、弥散分布,而传统可控气氛渗碳处理的齿轮碳化物较粗大。
[Abstract]:Carburizing of 18CrNi4A steel gear specimen was carried out in two ways: controllable atmosphere and low pressure vacuum. The effect of Carburizing mode on the structure of gear carburizing layer was studied. The results showed that the effective hardening layer depth was similar in the middle and middle teeth. Compared with controlled atmosphere Carburizing, the depth of effective hardening layer at the fillet of tooth root of low pressure vacuum Carburizing is significantly increased. However, the carbides of gears treated by conventional controlled atmosphere Carburizing are thicker.
【作者单位】： 哈尔滨东安发动机(集团)有限公司;哈尔滨工业大学材料科学与工程学院;
【分类号】：TG162.73

【相似文献】

相关期刊论文 前10条

1 王嘉琦;洪全;;中药渗碳[J];机械工人;1958年11期

2 Р.Е.глинер;刘水才;;对渗碳深度与渗碳时间之间关系的分析[J];国外化学热处理;1982年01期

3 王荣德;浅层渗碳[J];热加工工艺;1986年01期

4 张庚喜;;测定渗碳层深度应注意的几个问题[J];建筑机械;1987年05期

5 陈国英;杨蕴林;;钢的渗碳层深度与渗碳温度之间关系的数学模型[J];洛阳工学院学报;1990年04期

6 田白玉;关于渗碳层深度检测的探讨[J];机械工人;1996年12期

7 刘天佑,曲涛;高浓度渗碳及其应用[J];本溪冶金高等专科学校学报;2000年02期

8 程晓敏,陈铁群,游凤荷,王贵富;渗碳层电磁特性的数值模拟[J];武汉理工大学学报(信息与管理工程版);2000年05期

9 冯再新,张治民,乔俊强,张玲娟,周贤宾;直齿轮“渗碳-温挤”渗碳层厚度分布模型[J];材料科学与工艺;2002年02期

10 朱波,蔡s，

本文编号：1597874