激光焊接速度对焊缝组织和硬度分布的影响

发布时间：2018-03-14 05:23

  本文选题：不锈钢　切入点：激光焊　出处：《工程科学学报》2015年06期 　论文类型：期刊论文

【摘要】：利用激光焊接工艺焊接核级不锈钢,通过改变激光焊接速度得到不同的焊接接头.采用金相显微镜、扫描电子显微镜等手段研究了熔深比、δ/γ比、组织形貌以及焊缝中各相的成分.通过显微硬度测试了焊缝接头上硬度分布.随着焊接速度的增加,焊缝熔深比线性增加,焊缝中δ-铁素体含量增加,岛状组织增多,板条状组织增多,蠕虫状组织减少,焊缝区的平均硬度值增加.
[Abstract]:Using laser welding technology to weld nuclear grade stainless steel, different welding joints are obtained by changing laser welding speed. The penetration depth ratio and 未 / 纬 ratio are studied by means of metallographic microscope and scanning electron microscope. The microhardness distribution of the weld joint was measured by microhardness. With the increase of welding speed, the weld penetration ratio increased linearly, the 未-ferrite content in the weld increased, and the island structure increased. The average hardness of weld zone increased with the increase of strip structure, the decrease of wormlike structure and the increase of the average hardness of weld zone.
【作者单位】： 北京科技大学国家材料服役安全科学中心;
【分类号】：TG142.71

【相似文献】

相关会议论文 前6条

1 任大鹏;王小英;蔚拥军;李嵘;姜桂芬;郎定木;;不锈钢焊缝试样充氚后的显微组织[A];中国工程物理研究院科技年报（2002）[C];2002年

2 马海涛;王来;赵杰;韩双起;丛继功;李卫东;刘民;佟金杰;;汽油加氢装置反应器出口管线焊缝开裂原因分析[A];2007年中国机械工程学会年会论文集[C];2007年

3 任大鹏;罗德礼;李嵘;蔚勇军;郎定木;邱志聪;姜桂芬;;充氚不锈钢焊缝微观组织[A];中国核学会核材料分会2007年度学术交流会论文集[C];2007年

4 李琳;李继红;张敏;;预热温度对X100管线钢近焊缝区组织性能影响[A];第四届数控机床与自动化技术高层论坛论文集[C];2013年

5 郑洁;;摩托车手把管断裂问题的探讨(摘要)[A];四川省汽车工程学会第一届二次年会论文集[C];1991年

6 赵红凯;王春亮;任飞;刘兰霄;;钛合金焊接的研究进展[A];2007高技术新材料产业发展研讨会暨《材料导报》编委会年会论文集[C];2007年

相关硕士学位论文 前9条

1 张恒;5052铝合金激光焊接焊缝及其气孔研究[D];湖南大学;2013年

2 严岳胜;镍基合金薄板焊缝性能及旋压组织性能演变[D];中南大学;2012年

3 王晓国;R4s级系泊链闪光焊焊缝组织与性能研究[D];江苏科技大学;2010年

4 何金光;水电站月牙肋岔管组合焊缝分岔部位焊接温度场和残余应力研究[D];西南交通大学;2014年

5 高军义;T型管焊接变形数值仿真及其焊接工艺优化[D];新疆大学;2012年

6 宁勇;TC4钛合金激光焊接焊缝预测与成形质量分析[D];北京工业大学;2011年

7 刘爽;轨道客车转向架的激光电弧复合焊接性能研究[D];沈阳工业大学;2014年

8 王高见;ZS125-70型摩托车平叉焊接过程的数值模拟研究[D];重庆大学;2010年

9 兰天;铝/钛异种金属激光焊接研究[D];北京工业大学;2009年

，

本文编号：1609783