T91钢在碱金属氯化物介质中的高温腐蚀行为

发布时间：2018-03-15 03:14

  本文选题：T　切入点：生物质电厂　出处：《腐蚀与防护》2015年11期 　论文类型：期刊论文

【摘要】：模拟生物质电厂锅炉过热器的烟气侧环境,对过热器材料T91进行了高温腐蚀研究。采用试样腐蚀增重试验,测得了腐蚀动力学曲线;采用扫描电镜(SEM)、能谱仪(EDS)和X射线衍射仪(XRD)等,对T91试样腐蚀后的形貌、结构、元素含量和腐蚀产物的组成进行了分析。结果表明,T91的腐蚀对KCl蒸汽和反应温度比较敏感,随着温度的增高,腐蚀速率增加,腐蚀动力学曲线基本符合抛物线规律;T91的主要腐蚀产物为Fe_2O_3和(Fe_(0.6)Cr_(0.4)))2O)3,同时含有少量的Fe_3O_4和K_2Fe_4O_7。
[Abstract]:The high temperature corrosion of superheater material T91 was studied by simulating the flue gas side environment of boiler superheater in biomass power plant. The morphology, structure, element content and corrosion product composition of T91 specimens after corrosion were analyzed by means of SEM, EDS and XRD. The results showed that the corrosion of T91 was sensitive to KCl steam and reaction temperature. With the increase of temperature and corrosion rate, the corrosion kinetics curve basically accords with the parabola rule. The main corrosion products of T91 are Fe_2O_3 and Fetir / 0.6CrStg / Cr0. 4 / O / O / 3, and also contain a small amount of Fe_3O_4 and K\ + 2Fe4O\\ +\\ {7\}\%\%\%\%\%\%\%\%\%\%\%?
【作者单位】： 长沙理工大学化学与生物工程学院;广东电网公司电力科学研究院化学所;
【基金】：广东电网有限责任公司电力科学研究院项目(14430101000950)
【分类号】：TG142.1

【参考文献】

相关期刊论文 前2条

1 马海涛,郭贵芬,赵杰,王来;纯Fe在含KCl蒸汽的O_2气氛中的高温腐蚀行为[J];腐蚀科学与防护技术;2005年01期

2 孟庆若;;P92钢埋弧焊焊接工艺[J];焊接技术;2008年04期

【共引文献】

相关期刊论文 前6条

1 庞飞飞;李宇春;张锐锋;刘晓伟;曾维明;;620℃条件下T/P92耐热钢的腐蚀行为[J];腐蚀与防护;2013年12期

2 杨露;黄安国;杨格;杨东旭;;超超临界机组用T/P92钢焊接性能研究现状[J];电焊机;2014年05期

3 宋晓峰;;海上某油田热采腐蚀失效分析对稠油蒸汽吞吐工艺的研究[J];化学工程与装备;2014年12期

4 戴晟;曹德辉;李中华;詹白勺;;屏式过热器SA213-T92钢焊接工艺[J];焊接技术;2009年08期

5 吴益文;胡筱涛;任晨;吉静;;进口超超临界机组用耐高温P92钢管的检验[J];理化检验(物理分册);2012年10期

6 戴长清;田富强;轩福贞;;超超临界锅炉管道用T92/P92钢蠕变性能[J];压力容器;2010年03期

相关硕士学位论文 前1条

1 庞飞飞;T/P92新型铁素体耐热钢腐蚀行为研究[D];长沙理工大学;2013年

【二级参考文献】

相关期刊论文 前1条

1 李远士,牛焱,吴维_，

本文编号：1614175