700℃超超临界电站锅炉用高温合金617B和740H管道氩弧焊接头微观组织特征

发布时间：2018-03-20 18:42

  本文选题：B　切入点：H　出处：《稀有金属材料与工程》2015年09期 　论文类型：期刊论文

【摘要】：采用光学显微镜、扫描电镜、显微硬度计等手段,研究了617B和740H管道氩弧焊接头微观组织和显微硬度。结果表明:617B焊件焊缝晶粒外延生长明显,焊缝主要存在Mo、Ti元素偏析,枝晶间分布着不连续颗粒状碳化物M6C,焊缝硬度略高于母材。740H焊件焊缝主要存在Nb、Ti元素偏析,枝晶间有较多不规则颗粒状碳化物MC,没有观察到γ-γ′共晶相;热影响区晶粒稍有长大,晶内强化相γ′减少,晶界碳化物M23C6和MC发生回溶,焊缝硬度明显低于母材。
[Abstract]:The microstructure and microhardness of argon arc welding joints of 617B and 740H pipes were studied by means of optical microscope, scanning electron microscope and microhardness meter. There are discontinuous granular carbides M 6C distributed between dendrites, the hardness of weld is slightly higher than that of base metal. 740H welds are mainly segregated by NB Ti element, there are more irregular granular carbides MCs between dendrites, no 纬-纬 'eutectic phase is observed, and the grains in the heat affected zone grow slightly. With the decrease of 纬', the carbide M23C6 and MC of grain boundary are redissolved, and the hardness of weld is obviously lower than that of base metal.
【作者单位】： 北京科技大学;
【基金】：国家高技术研究发展计划(“863”计划)(2012AA03A501)
【分类号】：TG407

【参考文献】

相关期刊论文 前3条

1 毛健雄;;700℃超超临界机组高温材料研发的最新进展[J];电力建设;2013年08期

2 王珏;吴峗;董建新;张麦仓;谢锡善;徐芳泓;;700℃超超临界锅炉材料GH4700合金铸态组织及均匀化工艺[J];稀有金属材料与工程;2013年09期

3 江河;董建新;张麦仓;姚志浩;;700℃超超临界锅炉材料617B合金铸态组织及均匀化工艺[J];北京科技大学学报;2014年06期

【共引文献】

相关期刊论文 前10条

1 柳郁;;超超临界机组锅炉高温材料的选择和应用[J];科技创新与应用;2014年20期

2 L.O.Osoba;A.K.Khan;S.O.Adeosun;;Cracking Susceptibility After Post-Weld Heat Treatment in Haynes 282 Nickel Based Superalloy[J];Acta Metallurgica Sinica(English Letters);2013年06期

3 朱朝晖;;大厚度比镍基高温合金构件的焊接工艺[J];金属功能材料;2013年06期

4 王东雷;;700℃高效超超临界发电技术的研发现状及建议[J];科技视界;2014年36期

5 吴，

本文编号：1640333