超高强Cu-6.5Ni-1Al-1Si-0.15Mg-0.15Ce合金的淬火敏感性

发布时间：2018-03-22 10:02

  本文选题：CuNiAlSi合金　切入点：等温处理　出处：《中国有色金属学报》2015年06期 　论文类型：期刊论文

【摘要】：通过等温淬火方法获得Cu-6.5Ni-1Al-1Si-0.15Mg-0.15Ce合金的TTP曲线。采用硬度、电导率测试和透射电镜(TEM)观察等方法研究了等温温度和等温时间对合金性能和显微组织的影响。结果表明:合金TTP曲线的鼻尖温度约为675℃,淬火敏感区域为625~725℃;合金在650℃附近进行等温处理,δ-Ni2Si和共格的Ni3Al析出相的形核率和长大速率均很高;随着等温时间的延长,晶内析出的δ-Ni2Si和Ni3Al急剧粗化,同时,晶界处发生δ-Ni2Si的不连续析出,并形成无衬度析出带,导致合金经等温时效处理后硬度急剧下降,并且在鼻尖区具有很高的淬火敏感性。
[Abstract]:The TTP curves of Cu-6.5Ni-1Al-1Si-0.15Mg-0.15Ce alloy were obtained by isothermal quenching. The effects of isothermal temperature and isothermal time on the properties and microstructure of the alloy were studied by means of conductivity measurement and TEM observation. The results show that the nose tip temperature of the TTP curve of the alloy is about 675 鈩，