合金成分和奥氏体变形对粒状贝氏体和粒状组织转变的影响

发布时间：2018-05-02 09:08

  本文选题：合金成分 + 变形程度　； 参考：《钢铁研究学报》2015年05期

【摘要】：在Gleeble热模拟试验机上研究了低碳Mn-B系贝氏体钢的组织转变,分析了合金成分和奥氏体变形对粒状贝氏体及粒状组织转变的影响。结果表明,在相同冷却条件下,添加铬、铌元素后更利于粒状贝氏体组织的转变;在奥氏体未再结晶区,变形对粒状贝氏体及粒状组织的转变有明显的影响,随奥氏体变形温度的降低以及变形程度的增加,组织由粒状贝氏体向粒状组织变化。
[Abstract]:The microstructure transformation of low carbon Mn-B bainitic steel was studied on Gleeble thermal simulation machine. The effects of alloy composition and austenite deformation on granular bainite and granular microstructure transformation were analyzed. The results show that under the same cooling conditions, the addition of chromium and niobium is more favorable to the transformation of granular bainite, and in the unrecrystallized zone of austenite, the deformation has obvious influence on the transformation of granular bainite and granular structure. With the decrease of austenite deformation temperature and the increase of deformation degree, the microstructure changes from granular bainite to granular microstructure.
【作者单位】： 安徽工业大学冶金工程学院;
【基金】：科技部支撑计划资助项目(2007DAE30B04) 安徽省教育厅自然科学研究资助项目(KJ2013A061)
【分类号】：TG142.1

【相似文献】

相关期刊论文 前10条

1 江伯鸿;李鹏兴;马逸伟;潘素红;陆兴荣;;低碳低合金钢中粒状贝氏体的断裂特性[J];上海冶金;1980年01期

2 ;钢中的粒状贝氏体[J];钢铁;1983年06期

3 郭新成;;钢中的粒状贝氏体[J];金属热处理;1983年02期

4 林复中,丁玉然;粒状贝氏体组织对热锻模具钢性能的影响[J];机械工程材料;1985年01期

5 李智超,杨月君,王洪才;控制原始组织提高粒状贝氏体的机械性能[J];兵器材料科学与工程;1987年09期

6 王福明;李景慧;;粒状贝氏体的形貌分析[J];金属热处理学报;1991年03期

7 陈黄浦;粒状贝氏体的形变与断裂特征[J];金属学报;1992年05期

8 徐艳敏,胡社军;粒状贝氏体对20MnSi钢机械性能的影响[J];广州航海高等专科学校学报;1996年01期

9 乔斌;粒状贝氏体的形成[J];淮海工学院学报(自然科学版);1998年02期

10 赵捷,王志奇,李建平;低碳粒状贝氏体钢强韧化机理的探讨[J];天津理工学院学报;2000年01期

相关会议论文 前3条

1 吴保桥;罗双庆;;耐火H型钢屈服不明显原因初步分析[A];中国金属学会第一届青年学术年会论文集[C];2002年

2 谢崇津;刘卫斌;常红英;;粒状贝氏体钢25SiMoVB回火过程研究[A];第七届(2009)中国钢铁年会大会论文集(中)[C];2009年

3 岳重祥;刘东升;;沙钢高强韧易焊接特厚海工钢的研究开发[A];第五届中国船舶及海洋工程用钢发展论坛;2013船舶及海洋工程甲板舱室机械技术发展论坛论文集[C];2013年

相关硕士学位论文 前2条

1 蔡建伟;HSLA钢中M-A组织的形成动力学及其对力学性能的影响[D];燕山大学;2007年

2 苏金虎;2.25Cr-1Mo-0.25V钢锭的凝固组织及其在热锻过程中的演变[D];太原科技大学;2011年

，

本文编号：1833275