TC4激光立体成形显微组织对超声参量的影响

发布时间：2018-05-06 00:17

  本文选题：激光技术 + 激光立体成形　； 参考：《中国激光》2015年01期

【摘要】：以TC4钛合金激光立体成形件及锻件为研究对象,采用不同热处理制度对TC4钛合金激光立体成形件进行处理得到不同的热处理组织,并采用超声波无损检测方式获得超声波纵波声速和衰减系数,明晰超声参量和显微组织的相互作用机理。结果表明,不同的显微组织具有不同的超声波纵波声速和衰减系数;相比超声波纵波声速而言,衰减系数对TC4钛合金激光立体成形显微组织的变化更为灵敏。
[Abstract]:Taking TC4 titanium alloy laser solid forming parts and forgings as research objects, different heat treatment systems were used to treat TC4 titanium alloy laser solid forming parts and different heat treatment structures were obtained. The ultrasonic longitudinal wave velocity and attenuation coefficient are obtained by ultrasonic nondestructive testing, and the interaction mechanism between ultrasonic parameters and microstructure is clarified. The results show that different microstructures have different ultrasonic longitudinal wave velocities and attenuation coefficients, and the attenuation coefficients are more sensitive to the changes of laser forming microstructure of TC4 titanium alloys than those of ultrasonic longitudinal wave velocities.
【作者单位】： 西北工业大学凝固技术国家重点实验室;南昌航空大学轻合金加工科学与技术国防重点学科实验室;陕西工业职业技术学院;西安热工院有限公司;
【基金】：国家自然科学基金(51323008) 国家863计划(2013AA031103)
【分类号】：TG146.23;TG115.285

【参考文献】

相关期刊论文 前1条

1 张霜银;林鑫;陈静;黄卫东;;热处理对激光成形TC4合金组织及性能的影响[J];稀有金属材料与工程;2007年07期

【共引文献】

相关期刊论文 前10条

1 钟玉;屈金山;陈文静;潘全喜;;TC4钛合金电子束焊接头性能研究[J];焊接;2007年10期

2 何胜春;张田仓;;TC17钛合金惯性摩擦焊接头组织特征分析[J];焊接;2008年04期

3 洪志强;李萍;薛克敏;张青;;钛合金高温变形流变应力的预测[J];合肥工业大学学报(自然科学版);2007年08期

4 高永辉;李重河;国子明;庞威;鲁雄刚;丁伟中;钟庆东;;TiNi合金熔炼的耐火材料研究[J];过程工程学报;2010年S1期

5 吴巍;高洪明;吴林;;细晶粒钛合金粗晶区组织及接头力学性能分析[J];焊接学报;2008年01期

6 吴巍;高洪明;程广福;吴林;;细晶粒钛合金热影响区晶粒长大规律[J];焊接学报;2008年10期

7 周水亮;陶军;郭德伦;;细晶粒钛合金GTAW焊缝成形性能分析[J];焊接学报;2009年07期

8 周水亮;陶军;杜欲晓;郭德伦;;细晶粒钛合金薄板TIG焊温度场分析[J];焊接学报;2010年12期

9 王锦林;甘章华;陈义明;肖建中;;不同冷却速度对Ti-6Al-4V钛合金热模拟试样组织的影响[J];焊接学报;2011年08期

10 刘红;洪贺;范s，

本文编号：1849915