Ti-Nb复合微合金化高强钢连续冷却转变曲线

发布时间：2018-05-09 15:52

  本文选题：热膨胀曲线 + CCT曲线　； 参考：《热加工工艺》2015年24期

【摘要】：通过在热模拟试验机上探究不同冷却速率对Ti-Nb复合微合金化高强钢组织和相变的影响,研究了Ti-Nb复合微合金化高强钢的连续冷却转变(CCT)过程。结果表明,不同冷却速率下分别得到铁素体+珠光体、贝氏体和马氏体组织。根据热膨胀曲线和实验钢组织绘制了CCT曲线,为研究钢种的固态相变过程、加工工艺以及热处理工艺提供依据。
[Abstract]:The effect of different cooling rates on the microstructure and phase transformation of Ti-Nb composite microalloyed high strength steel was investigated on a thermal simulation machine. The continuous cooling transformation process of Ti-Nb composite microalloyed high strength steel was studied. The results showed that ferrite pearlite bainite and martensite were obtained at different cooling rates. The CCT curves were drawn according to the thermal expansion curve and the structure of the experimental steel, which provided the basis for the study of the solid phase transformation process, the processing technology and the heat treatment process of the steel.
【作者单位】： 武汉钢铁(集团)公司研究院;
【分类号】：TG142.1

【相似文献】

相关期刊论文 前10条

1 许峰云;;第八届固态相变、凝固及应用学术会议在上海召开[J];金属热处理;2008年12期

2 ;第九届全国固态相变、凝固及应用学术会议[J];金属热处理;2010年02期

3 缪成亮;;第九届固态相变与凝固及应用学术会议在宁波召开[J];金属热处理;2010年06期

4 徐祖耀;;1981年国际固态相变会议概况[J];上海金属.有色分册;1982年01期

5 常辉;周廉;张廷杰;;钛合金固态相变的研究进展[J];稀有金属材料与工程;2007年09期

6 任晓;周文龙;陈国清;吴承伟;黄朝晖;张俊善;;稳恒强磁场在固态相变中应用的研究进展[J];材料工程;2009年03期

7 缪成亮;;第九届固态相变与凝固及应用学术会议在宁波胜利召开[J];材料热处理学报;2010年06期

8 ;新书《金属固态相变教程》介绍[J];热处理;2011年02期

9 曹梅青;崔洪芝;孙宏飞;宋强;;《金属固态相变原理》教学改革初探[J];科技视界;2012年28期

10 高宁;固态相变的动力学模型[J];金属热处理学报;1998年04期

相关会议论文 前3条

1 邵晖;葛鹏;赵永庆;曾卫东;王凯旋;周伟;杨义;;TB6钛合金降温时温度场模拟及固态相变[A];第十四届全国钛及钛合金学术交流会论文集（上册）[C];2010年

2 陈水源;沈博彦;;Y-PSZ氧化锆的t'→c'相变化[A];海峡两岸电子显微学研讨会论文专集[C];1992年

3 龙木军;董志华;陈登福;张星;盛俊豪;陈春梅;;连铸坯固态相变中奥氏体溶解行为研究[A];第十七届（2013年）全国冶金反应工程学学术会议论文集（上册）[C];2013年

相关博士学位论文 前2条

1 励志峰;强磁场下AZ91合金固态相变行为研究[D];上海交通大学;2008年

2 袁泉;机械驱动及放电条件下Ti-C-N体系的固态相变[D];南京航空航天大学;2012年

相关硕士学位论文 前2条

1 赵万祺;高压对Al-20Mg合金固态相变及力学性能影响[D];哈尔滨工业大学;2015年

2 李纪锋;单晶锆固态相变与熔化特性的分子动力学模拟研究[D];中国工程物理研究院;2014年

，

本文编号：1866620