线能量对奥氏体不锈钢激光焊接质量的影响

发布时间：2018-05-14 20:07

  本文选题：激光技术 + 奥氏体不锈钢　； 参考：《激光技术》2015年06期

【摘要】：为了研究线能量对304奥氏体不锈钢激光焊接质量的影响,采用高功率Nd∶YAG激光器及焊接机器人对304奥氏体不锈钢薄板进行了激光焊接工艺试验,并使用光学显微镜、显微硬度计、拉伸试验机等仪器重点研究了线能量对304奥氏体不锈钢激光焊接焊缝成形和力学性能的影响。结果表明,线能量对焊缝成形、显微硬度及力学性能有较大影响,接头显微硬度分布不均匀,低功率时静拉伸强度最小值为671.67MPa,高功率时静拉伸强度最小值达780MPa。
[Abstract]:In order to study the effect of linear energy on the laser welding quality of 304 austenitic stainless steel, the laser welding process of 304 austenitic stainless steel sheet was tested by high power Nd:YAG laser and welding robot, and the optical microscope was used. The influence of linear energy on weld formation and mechanical properties of 304 austenitic stainless steel by laser welding was studied by means of microhardness tester and tensile tester. The results show that the linear energy has a great influence on the weld formation, microhardness and mechanical properties. The microhardness distribution of the joint is not uniform. The minimum value of static tensile strength at low power is 671.67 MPA, and the minimum value of static tensile strength at high power is 780 MPA.
【作者单位】： 长春理工大学机电工程学院;
【基金】：吉林省科技支撑计划重点资助项目(20120353)
【分类号】：TG456.7

【参考文献】

相关期刊论文 前10条

1 单际国;雷祥;谭稳达;张红军;陈武柱;任家烈;;AZ31B变形镁合金CO_2激光焊接模式及焊缝成形特点[J];焊接学报;2008年04期

2 张林杰;张建勋;曹伟杰;柴国明;巩水利;;工艺参数对304不锈钢脉冲Nd:YAG激光/TIG电弧复合焊焊缝成形的影响[J];焊接学报;2011年01期

3 王蔚;陈俐;赵兴科;黄继华;;激光焊接工艺参数对NiTi形状记忆合金焊缝成形的影响[J];中国激光;2008年02期

4 吴世凯;肖荣诗;陈铠;;大厚度不锈钢板的激光焊接[J];中国激光;2009年09期

5 石岩;刘佳;张宏;;20Cr2Ni4A-20g异种钢Slab CO_2激光深熔焊接工艺研究[J];中国激光;2011年06期

6 刘佳;张宏;石岩;;基于Design-Expert V7设计的不锈钢激光非熔透搭接焊工艺优化研究[J];机械工程学报;2011年16期

7 徐磊;刘西霞;李庆福;胡光蓉;张屹;;高强镀锌钢激光填粉焊接工艺试验研究[J];激光技术;2014年01期

8 李建敏;王春明;闫飞;胡席远;吴圣川;张威;;6005A激光-MIG复合焊接头组织及力学性能研究[J];激光技术;2014年06期

9 许飞;杨t，

本文编号：1889281