阀杆断裂分析

发布时间：2018-05-21 05:15

  本文选题：失效 + 阀杆　； 参考：《热加工工艺》2015年24期

【摘要】：对阀杆进行宏观检查、金相显微组织观察、化学成分分析、硬度测试试验和拉伸试验,结果表明:该阀杆因为同时受到交变应力和附加弯曲应力的共同作用,在阀杆外表面处产生微裂纹,微裂纹逐渐扩展,致使阀杆的有效承载面积逐步缩小,直至发生断裂。阀杆断裂的主要原因是:阀杆的硬度偏高,强度偏低,力学性能不符合要求,而且长期在高应力的交替作用下导致其发生疲劳断裂。
[Abstract]:Macroscopical inspection, metallographic microstructure observation, chemical composition analysis, hardness test and tensile test show that the stem is subjected to both alternating stress and additional bending stress at the same time. Microcracks appear on the outer surface of the stem, and the microcracks expand gradually, which results in the effective bearing area of the stem gradually shrinking until fracture occurs. The main reason of stem fracture is that the valve stem has high hardness and low strength, and its mechanical properties do not meet the requirements, and the fatigue fracture occurs under the alternating action of high stress for a long time.
【作者单位】： 龙岩学院物理与机电工程学院;
【分类号】：TG115

【相似文献】

相关期刊论文 前10条

1 孟繁增;;阀杆氮化事故分析[J];机械工人;1989年11期

2 张明友;;柴油机排气阀杆断裂失效研究[J];武汉工学院学报;1992年03期

3 李妙珍;张葵东;;阀杆与阀头的焊接问题[J];石家庄职业技术学院学报;2006年04期

4 冷启霜;;某电厂阀杆断裂原因分析[J];机械工程师;2010年08期

5 王勇;季华建;文佳卉;陈海;;压缩机电动阀阀杆断裂原因分析[J];理化检验(物理分册);2013年04期

6 李泽民,嘉赵宾;气阀阀杆简易倒角装置[J];机械工人.冷加工;1991年12期

7 戴乐阳;林少芬;陈清林;段振;;排气阀杆早期断裂失效分析[J];热加工工艺;2010年22期

8 杨昱;阎保秋;;细长阀杆热处理淬火的工装设计[J];金属加工(热加工);2014年15期

9 矫永臣;;阀杆与方头处断裂原因及处理[J];金属加工(热加工);2012年12期

10 刘永样;;黄铜阀顶和不锈钢阀杆的氧—乙炔焰钎焊[J];焊接;1976年06期

相关会议论文 前2条

1 王领;吕鹏飞;郭宏伟;阿尔达克;;新疆油田公司某天然气处理站阀杆断裂分析[A];2011年全国机械行业可靠性技术学术交流会暨第四届可靠性工程分会第三次全体委员大会论文集[C];2011年

2 倪兆荣;李志章;;输气管道阀门阀杆及阀套螺纹失效分析及磨损机理研究[A];第九次全国热处理大会论文集（一）[C];2007年

，

本文编号：1917889