铝合金三元气体保护焊工艺

发布时间：2018-05-21 11:30

  本文选题：三元保护气体 + 铝合金　； 参考：《焊接》2015年10期

【摘要】：氩氦氮三元混合气体保护焊工艺在铝合金焊接中表现出一定的性能优势。文中从电弧电信号、温度场特征等方面进行系统测试,总结三元保护气焊与纯氩保护气焊的技术特点差异,测试分析三元混合气体保护焊的冲击韧性、接头硬度、微观组织,与纯氩保护焊进行对比。试验结果及实际焊工操作表明,三元气体保护焊电弧更为集中稳定,焊接接头韧性更高,气孔率更低,接头软化改善明显,焊接熔深增大,电弧更易控制,可以获得优良的焊接接头。
[Abstract]:Argon helium nitrogen three element mixed gas shielded welding technology shows a certain performance advantage in aluminum alloy welding. In this paper, the characteristics of electric arc signal and temperature field are systematically tested. The difference between three element protection gas welding and pure argon protection welding is summarized, and the impact toughness and joint hardness of the three element gas shielded welding are tested and analyzed. The microstructure is compared with the pure argon shielded welding. The results of the test and the actual welder operation show that the three element gas arc welding arc is more concentrated, the welding joint toughness is higher, the porosity is lower, the joint softening is improved obviously, the welding depth is increased, the arc is more easily controlled, and the excellent welding joint can be obtained.
【作者单位】： 南车青岛四方机车车辆股份有限公司;
【基金】：四方股份工艺开发项目(2014.315)
【分类号】：TG444.72

【相似文献】

相关期刊论文 前10条

1 陈丽丽,李学伟;CO_2气体保护焊在我公司的推广及应用[J];煤矿机械;2002年08期

2 蔚红;;CO_2气体保护焊平板对接操作技巧[J];包头职业技术学院学报;2005年03期

3 魏国;;CO_2气体保护焊飞溅产生的原因及减少措施[J];机械工人;2006年06期

4 刘俊良;刘社琴;曾祥泉;;减少CO_2气体保护焊飞溅的方法[J];机械工人;2006年11期

5 ;CO_2气体保护焊对电源有什么要求[J];电焊机;2007年08期

6 彭存岭;刘洪章;贾征;李小松;赵书全;;浅谈CO_2气体保护焊接中的几个问题[J];锅炉制造;2009年06期

7 孙明越;;浅谈CO_2气体保护焊产生飞溅的原因及控制措施[J];硅谷;2010年05期

8 王绪桥;;CO_2气体保护焊工艺应用[J];金属加工(热加工);2010年10期

9 孙子建;;苏联CO_2气体保护焊接会媝侧，

本文编号：1919016