45钢半轴套管锻件端面撕裂原因分析

发布时间：2018-06-07 07:42

  本文选题：套管锻件 + 撕裂　； 参考：《金属热处理》2015年12期

【摘要】：对45钢半轴套管锻件开裂原因进行了分析。结果表明,失效锻件开裂原因是由于棒料的加热温度过高,造成材料组织严重过热,甚至出现过烧特征的晶间熔洞组织。组织中晶间结合力急剧降低,锻造应力已经大于此时材料的抗破断强度,因而造成沿晶开裂的热裂纹,裂纹继续向端面扩展撕裂。由于锻造工艺不当,锻件端面外边缘形成尖角,该处的冷却速度加大,裂纹的撕裂断口由沿晶转变为穿晶,而且随着温度的降低,氧化脱碳也逐渐减弱。
[Abstract]:The cracking causes of 45 steel semi-shaft casing forgings are analyzed. The results show that the cracking of the invalid forgings is due to the excessive heating temperature of the bar, which results in the serious overheating of the material structure and even the appearance of the intergranular melting structure with the characteristics of overburning. The intergranular bonding force in the microstructure decreases sharply and the forging stress is higher than the breaking strength of the material at this time, which results in the thermal crack of intergranular cracking and the crack continues to propagate and tear to the end face. Due to the improper forging process, the outer edge of the forgings formed sharp angle, the cooling rate increased, the crack tear fracture changed from intergranular to transgranular, and the oxidation decarbonization gradually weakened with the decrease of temperature.
【作者单位】： 合肥市建元机械有限责任公司;温州永工热处理有限公司;江苏特龙驱动轴制造有限公司;
【分类号】：U466;TG316

【共引文献】

相关期刊论文 前10条

1 赵麦群,张颢,武占学;泥浆泵重载齿轮用中碳易削钢的试验研究[J];兵器材料科学与工程;2003年05期

2 韩继铖,李解,王秀,乔光;连铸坯夹杂的调查与防止[J];包钢科技;2001年03期

3 卢翔宇,李波,王永顺,赵保国;喂Ca-Si丝对钢中夹杂物变性的研究[J];包钢科技;2003年S1期

4 王惠,赵俊华,赵文祥,吴国定,叶锐华;铸造铝镍钴磁钢的冶金质量分析[J];北京钢铁学院学报;1987年03期

5 张丽娜,张麦仓,李晓,董建新,谢锡善;P/M Rene95合金夹杂物微观力学行为观察[J];北京科技大学学报;2002年04期

6 吕彦,杨吉春,李波,张芳;Ca-RE复合处理对钢中硫化物的影响[J];包头钢铁学院学报;2004年02期

7 霍文霞;计云萍;金自力;任慧平;;稀土对耐磨铸钢中夹杂物影响机理的研究[J];内蒙古科技大学学报;2011年04期

8 卢献忠;吴润;吴海涛;黄雷;;钢中硫化物的形成及作用研究进展[J];材料导报;2010年13期

9 张伟;徐玉松;陆敏松;李国一;;电渣重熔马氏体时效钢中的非金属夹杂物研究[J];材料开发与应用;2010年02期

10 任海鹏,张万显,阎振h，

本文编号：1990392