发布时间：2018-06-19 22:04

  本文选题：无抑制剂取向硅钢 + 初次再结晶退火　； 参考：《材料热处理学报》2015年S2期

【摘要】：在实验室中采用无抑制剂法制备取向硅钢,利用XRD、TEM等方法研究了冷轧和初次再结晶阶段的微观组织与织构。结果表明,冷轧板织构主要由α织构和γ织构组成;初次再结晶退火后α织构减弱,γ面织构{111}112增加,初次再结晶退火70 s后出现Goss织构。EBSD分析显示Goss位向晶粒大多与{111}112位向晶粒相邻;随退火时间的增加,Goss和{111}112位向晶粒均有所增加。
[Abstract]:The oriented silicon steel was prepared by non-inhibitor method in laboratory. The microstructure and texture of cold rolling and primary recrystallization were studied by means of XRD- TEM. The results show that the texture of cold rolled sheet is mainly composed of 伪 texture and 纬 texture, the 伪 texture decreases and the 纬 plane texture {111} 112 increases after primary recrystallization annealing. After initial recrystallization annealing for 70 s, Goss texture. EBSD analysis showed that most of the Goss orientation grains were adjacent to {111} 112 orientation grains, and both Goss and {111} 112 orientation grains increased with the increase of annealing time.
【作者单位】： 安泰科技股份有限公司功能材料事业部;中国钢研科技集团有限公司;
【分类号】：TG335;TG161;TG142.1

【相似文献】

相关期刊论文 前10条

1 吴润;杨琴;刘浩;黄青武;黄闽津;胡斌;郭玉娜;;高强冷轧铌钢的再结晶退火与性能模型[J];武汉科技大学学报(自然科学版);2008年03期

2 ;感应无氧化再结晶退火[J];金属材料与热加工工艺;1979年02期

3 张文秀;用再结晶退火法消除蛇形管托架的冲压裂纹[J];金属热处理;1996年04期

4 刘大利;张聪惠;李中奎;周军;石明华;田锋;;Zr-Sn-Nb-Fe合金加工过程中再结晶退火处理研究[J];稀有金属;2012年02期

5 王定祥;;卷板的远红外再结晶退火[J];水利电力机械;1986年06期

6 魏勤;卫婷;宋广三;;声双折射法研究再结晶退火处理对45#钢微观组织的影响[J];应用声学;2011年03期

7 张永晖,彭大暑,张辉;快速再结晶退火过程金属晶粒度的计算[J];热加工工艺;2001年02期

8 刘磊;齐锦刚;赵作福;王家毅;杨海明;王建中;;电脉冲作用下硅黄铜再结晶退火的工艺研究[J];辽宁工业大学学报(自然科学版);2013年04期

9 池国明;3A21铝合金板带材再结晶退火组织性能的研究[J];轻合金加工技术;2001年08期

10 李文学;华连庚;李德超;;稀土铝箔再结晶退火组织、织构研究[J];轻合金加工技术;2010年11期

相关会议论文 前6条

1 刘浩;余晓静;彭涛;;再结晶退火对含磷冷轧高强度钢板显微组织的影响[A];2005年全国冷轧板带生产技术交流会暨第三届薄钢板质量研讨会论文集[C];2005年

2 刘晓菊;贾真;邵芬;薛庆贺;杜雪卉;;冷变形对1700MPa级别高强度钢组织性能影响的研究[A];陕西省机械工程学会理化检验分会第九届年会论文集[C];2013年

3 张素勤;李国俊;陈复民;;最终再结晶退火温度对锡磷青铜带材组织、性能的影响[A];第四届金属材料及热处理年会论文集（下）[C];1991年

4 孙威;江自应;;Al-RE合金再结晶退火后的晶界内耗及相应晶界的TEM观察[A];内耗与超声衰减——第二次全国固体内耗与超声衰减学术会议论文集[C];1988年

5 陈s，

本文编号：2041481