pH值对304不锈钢在3.5%NaCl溶液中点蚀过程的影响

发布时间：2018-06-22 04:59

  本文选题：不锈钢 + pH值　； 参考：《中国腐蚀与防护学报》2015年01期

【摘要】：采用恒电位极化及三维视频显微技术研究不同pH值对304不锈钢在3.5%NaCl溶液中单个蚀孔的点蚀动力学及腐蚀形貌特征的影响。结果表明,当pH值等于1,4,7,10和14,极化电位为0.15VvsSCE时,单个蚀孔的点蚀电流、蚀孔体积、深度及孔口直径的增加速率随pH值的降低而增大。在同一pH值下,孔深的增加速率随时间的延长而增大,孔口直径的增加速率随时间的延长而减小。不同pH值下,单个蚀孔的生长均受腐蚀产物扩散控制。蚀孔表面为多孔花边盖,并且花边盖板的完整度随pH值的降低而下降。
[Abstract]:The effects of different pH values on the pitting kinetics and corrosion morphology of 304 stainless steel in 3.5 NaCl solution were studied by potentiostatic polarization and 3D video microscopy. The results show that the pitting current, pore volume, depth and pore diameter increase with the decrease of pH value when pH is equal to 1 ~ 4 ~ 4 ~ 7 ~ 10 and 14, and the polarization potential is 0.15 V / s SCE. At the same pH value, the increase rate of pore depth increases with time, and the increase rate of pore diameter decreases with time. At different pH values, the growth of a single pore is controlled by the diffusion of corrosion products. The surface of the etched hole is a porous lace cover, and the integrity of the lace cover plate decreases with the decrease of pH value.
【作者单位】： 南昌航空大学轻合金加工科学与技术国防重点学科实验室;北京航空航天大学材料科学与工程学院;中航工业成飞制造工程部;
【基金】：国家自然科学基金项目(51071083)资助
【分类号】：TG142.71;TG172

【参考文献】

相关期刊论文 前4条

1 龚小芝,肖娟,左禹,赵景茂,熊金平;溶液pH值对不锈钢亚稳态孔蚀行为的影响[J];北京化工大学学报(自然科学版);2002年04期

2 梁成浩，高扬;304不锈钢敏化热处理对耐蚀性的影响[J];化工机械;1995年02期

3 唐子龙;孔蚀发展过程动力学分析[J];中国腐蚀与防护学报;1998年04期

4 孙道明;蒋益明;高娟;项秋伟;龚佳;李劲;;不锈钢点蚀花边盖脱落与稳定生长[J];郑州大学学报(工学版);2009年01期

【共引文献】

相关期刊论文 前10条

1 李潇;施雯;张健;陈智勇;;非平衡磁控溅射CrTiAlN涂层的耐腐蚀性能[J];中国表面工程;2010年03期

2 叶超;杜楠;赵晴;田文明;;不锈钢点蚀行为及研究方法的进展[J];腐蚀与防护;2014年03期

3 杜楠;叶超;田文明;赵晴;;304不锈钢点蚀行为的电化学阻抗谱研究[J];材料工程;2014年06期

4 艾莹s，

本文编号：2051682