Zn在模拟酸雨大气环境中的腐蚀行为

发布时间：2018-06-28 17:15

  本文选题：模拟酸雨 + 大气腐蚀　； 参考：《中国有色金属学报》2015年02期

【摘要】：利用自制的降雨喷淋装置模拟Zn在酸雨条件下的大气腐蚀行为,采用扫描电镜(SEM)、X射线能谱(EDS)、X射线衍射(XRD)和电化学测试技术分别研究Zn腐蚀48、96、144、192和240 h后的腐蚀产物成分、锈层截面形貌以及表面锈层的电化学特性,分析了锈层对Zn腐蚀行为的影响。结果表明:主要的腐蚀产物为Zn(OH)2、Zn SO4、Zn4SO4(OH)6·3H2O和Zn5(OH)8Cl2·H2O;腐蚀过程中,Zn的表面形成了具有较好保护性的锈层,随着腐蚀时间的延长,锈层对Zn的保护作用先增强后减弱。
[Abstract]:The atmospheric corrosion behavior of Zn in acid rain was simulated by a self-made rainfall sprinkler. The composition of Zn corrosion products after 489 614 4192 and 240 h corrosion were studied by means of scanning electron microscopy (SEM) and X-ray diffraction (XRD) and electrochemical measurement techniques, respectively. The effect of rust layer on the corrosion behavior of Zn was analyzed. The results show that the main corrosion products are Zn (OH) 2n so 4 (OH) 4SO 4 (OH) 63H 2O and Zn 5 (OH) 8Cl 2 H 2O, and a protective rust layer is formed on the surface of Zn in the process of corrosion. With the prolongation of the corrosion time, the protective effect of the rust layer on Zn is first enhanced and then weakened.
【作者单位】： 中国科学院金属研究所;广东电网公司电力科学研究院;
【基金】：南网科技项目(K-GD2014-0532) 国防技术资助项目(H102011B002)
【分类号】：TG172.3;TG146.13

【参考文献】

相关期刊论文 前8条

1 ;Corrosion behavior and mechanism of the automotive hot-dip galvanized steel with alkaline mud adhesion[J];International Journal of Minerals Metallurgy and Materials;2009年04期

2 默增禄,程志云;输电线路杆塔的腐蚀与防治对策[J];电力建设;2004年01期

3 宋卓;郭军科;郭锦龙;;环境对电网材料的腐蚀影响分析及评价[J];山西电力;2008年05期

4 严川伟,史志明,林海潮,曹楚南;Zn在SO_2环境中大气腐蚀初期表面特性研究[J];腐蚀科学与防护技术;2000年03期

5 王振尧,于国才,韩薇;我国若干典型大气环境中的锌腐蚀[J];腐蚀科学与防护技术;2003年04期

6 黎学明;刘强;孔令峰;周建庭;;模拟酸雨溶液中应力对镀锌钢绞线腐蚀行为影响[J];腐蚀科学与防护技术;2008年01期

7 谈天;陈彤;张俊喜;邢逸俊;洪毅成;;镀锌钢在模拟不同服役环境中的腐蚀行为[J];腐蚀与防护;2014年04期

8 许新辉;郜洪文;;中国南方酸雨的分布特征及其成因分析[J];四川环境;2011年04期

【共引文献】

相关期刊论文 前10条

1 张s，

本文编号：2078753