酸化缓蚀剂的缓蚀作用机理研究

发布时间：2018-07-06 11:34

  本文选题：酸化缓蚀剂 + 缓蚀效率　； 参考：《西安石油大学学报(自然科学版)》2015年01期

【摘要】：通过模拟酸化腐蚀实验,评价马氏体不锈钢油管用酸化缓蚀剂的缓蚀性能。同时,利用电化学测试技术,探讨其在不同温度条件下的缓蚀作用机理。结果表明:超级13Cr马氏体不锈钢在120℃鲜酸中的均匀腐蚀速率仅为14.551 6 mm/a,远小于50.8 mm/a,缓蚀效率在90%以上,并且局部腐蚀轻微,表明酸化缓蚀剂与超级13Cr马氏体不锈钢具有良好的匹配性。在30℃和60℃,添加缓蚀剂后,腐蚀电位正移,缓蚀剂作用机理为"负催化效应型"。在80℃,腐蚀电位负移,缓蚀剂作用机理为"几何覆盖效应型"。
[Abstract]:The corrosion inhibition performance of the acid corrosion inhibitor for martensitic stainless steel tubing was evaluated by simulated acid corrosion test. At the same time, the mechanism of corrosion inhibition under different temperature conditions was investigated by electrochemical testing technology. The results showed that the uniform corrosion rate of super 13Cr martensitic stainless steel in fresh acid at 120 C was only 14.5516 mm/a, far less than 50.8. Mm/a, the corrosion inhibition efficiency is above 90%, and the local corrosion is slight, indicating that the acid corrosion inhibitor has a good match with the super 13Cr martensitic stainless steel. After adding corrosion inhibitor at 30 and 60, the corrosion potential is shifted positively, the mechanism of corrosion inhibitor is "negative catalytic effect". The corrosion potential is negative shift at 80, and the mechanism of corrosion inhibitor is "geometric coverage". Effect type.
【作者单位】： 中海石油(中国)有限公司湛江分公司;
【基金】：国家自然科学基金项目(编号:51271146)
【分类号】：TG174.42

【共引文献】

相关博士学位论文 前10条

1 常雪婷;海洋优势菌种附着腐蚀Fe_3Al及其复合材料界面与机理研究[D];中国海洋大学;2010年

2 王洪芬;涉海抗菌耐蚀性TiO_2复合薄膜的制备及其性能研究[D];中国海洋大学;2010年

3 王爱萍;改性纳米二氧化钛薄膜制备及其在模拟海水中光生阴极保护性能研究[D];中国海洋大学;2010年

4 刘春侠;锗在锌电积中的行为及添加剂作用的研究[D];昆明理工大学;2008年

5 张启波;咪唑基离子液体在锌电沉积中的作用机理研究[D];昆明理工大学;2010年

6 蒋雪松;用于有机磷农药残留检测的免疫生物传感器的研究[D];浙江大学;2008年

7 黄君冉;用于农药残留检测的压电免疫生物传感器的研究[D];浙江大学;2010年

8 王鹤峰;不锈钢表面氮掺杂二氧化钛薄膜的制备及其性能研究[D];太原理工大学;2011年

9 沈羽;固体氧化物燃料电池阳极及连接材料的制备与性能研究[D];吉林大学;2011年

10 刘一婷;基于酞菁铜的太阳能电池的研究[D];大连理工大学;2011年

【相似文献】

相关期刊论文 前10条

1 郑家q，

本文编号：2102647