碳当量对高压油缸端盖球铁件组织性能的影响

发布时间：2018-07-09 16:27

  本文选题：碳当量 + 高压油缸端盖　； 参考：《铸造技术》2015年12期

【摘要】：浇注了不同碳当量的高压油缸端盖球铁件,采用金相、拉伸和硬度测试方法,分析了铸件石墨形态、球化率和力学性能。研究结果表明:碳当量在4.03%~4.17%范围时,随着碳当量的升高,石墨的圆整度明显增加;当碳当量达到4.31%时,石墨出现衰退现象。碳当量为4.17%时,高压油缸端盖铸件的抗拉强度和硬度值达到峰值,分别为585 MPa和234 HB。高压油缸端盖铸件的屈服强度随着碳当量的增加呈减小趋势,碳当量从4.03%增加到4.31%时,屈服强度从480 MPa降至358 MPa。
[Abstract]:The graphite morphology, spheroidizing and mechanical properties of the castings were analyzed with metallographic, tensile and hardness testing methods. The results showed that when carbon equivalent increased in the range of 4.03%~4.17%, the roundness of graphite increased obviously with the increase of carbon equivalent in the range of 4.03%~4.17%; when the carbon equivalent reached 4.31%, the graphite appeared to decline. When the carbon equivalent is 4.17%, the tensile strength and hardness of the end cap castings of the high pressure oil cylinder reach the peak value. The yield strength of the end cover castings of 585 MPa and 234 HB. high pressure oil cylinder decreases with the increase of carbon equivalent, and the yield strength decreases from 480 MPa to 358 MPa. when the carbon equivalent increases from 4.03% to 4.31%.
【作者单位】： 常州大学江苏省材料表面工程技术重点实验室;常州轻工技术职业学院机械工程系;江苏恒立高压油缸股份有限公司;
【基金】：江苏省科技成果转化资助项目(BA2013078)
【分类号】：TG255

【相似文献】

相关期刊论文 前10条

1 丁鸿远 ,谭弼臣;碳当量是什麽意思?粘土的粘性和膨胀性怎样试验?[J];铸工;1954年01期

2 温建峰;16Mn钢碳当量、规格、性能优化[J];宽厚板;1995年01期

3 黎振华,李言祥,耿慧远;工艺因素对热分析碳当量仪测试结果影响的研究[J];铸造;2004年12期

4 曹良裕,魏战江;钢的碳当量公式及其在焊接中的应用[J];材料开发与应用;1999年01期

5 杨贵成;感应电炉熔炼灰铸铁的碳当量与抗拉强度和硬度的关系[J];铸造设备研究;2002年04期

6 王晓香;管线钢焊接常用的几种碳当量公式[J];焊管;2004年02期

7 张小雪;刘兰俊;李永红;;微合金化对高碳当量灰铁组织的影响[J];铸造技术;2012年07期

8 孙业瓒，车胜锡，，陈洪升，安阁英;铸铁样杯的结构参数对碳当量预测精度的影响[J];中国铸机;1995年02期

9 李明泉;;研究“碳当量”“共晶度”的指导意义[J];铸造技术;1985年03期

10 盛达,黄惠松,曾效舒,王昆林,刘金城,曾大本;稀土高碳当量灰口铸铁组织与性能的研究[J];清华大学学报(自然科学版);1987年05期

相关重要报纸文章 前1条

1 清华大学国情研究中心主任 胡鞍钢;中国绿色现代化“三步走”[N];中国远洋报;2010年

相关硕士学位论文 前1条

1 许丹奇;二汽车保安铸件的碳当量研究与生产实践[D];华中师范大学;2006年

本文编号：2109946