低温多向锻造锆-4合金的力学性能和超细晶组织演化（英文）

发布时间：2018-07-17 15:42

【摘要】：研究低温(77K)多向锻造锆-4合金累积应变为1.48,2.96,4.44和5.91时的力学性能和组织演变。通过万能拉伸测试和维氏硬度实验测得多向锻造合金的力学性能。相对于原始合金,当锆-4合金变形的累积变形为5.91时,其极限抗拉强度从474MPa提高到717MPa,维氏硬度从HV 190提高到HV 238。然而,由于锆-4合金的低应变硬化,其延展性显著降低(18%~3.5%)。变形合金强度和硬度的提高是因为多向锻造引起的晶粒尺寸效应和高的位错密度。采用光学显微镜和透射电镜表征变形试样的显微组织演化。当累积应变为5.91时,经12次多向锻造后合金的微观组织演化主要是超细晶的形成,其平均晶粒尺寸为150~250nm。
[Abstract]:The mechanical properties and microstructure evolution of the multi - directionally forged zirconium - 4 alloy at low temperature ( 77K ) were investigated . The mechanical properties and microstructure evolution of multi - directionally forged alloys were measured by universal tensile test and Vickers hardness test .
【作者单位】： Department
【基金】：BRNS,Bombay for their financial grant to this work through grant No.BRN-577-MMD
【分类号】：TG319;TG146.414

【参考文献】

相关期刊论文 前1条

1 ;Effects of Strain Rate and Deformation Temperature on Microstructures and Hardness in Plastically Deformed Pure Aluminum[J];Journal of Materials Science & Technology;2011年01期

【共引文献】

相关期刊论文 前10条

1 徐宏海;阎红娟;李新民;;刀具材料深冷处理研究现状及发展趋势[J];材料导报;2008年S2期

2 刘嘎;王伯健;师晓莉;白鹤;徐萍;;冷拉珠光体钢丝的加工硬化及组织性能演变研究现状[J];材料导报;2008年S2期

3 许晓嫦;张孜昭;胡楠;;变形程度对强变形Al-4%Cu合金退火组织性能的影响[J];材料科学与工艺;2011年02期

4 李晓;李萍;王成;张倩倩;;基于SPD法颗粒增强铝基复合材料研究综述[J];粉末冶金工业;2011年01期

5 刘润;周蕾;王军丽;;异步叠轧制备超细晶材料的研究进展[J];材料导报;2013年01期

6 史昆玉;沈涛;陈春浩;薛丽红;严有为;;高能球磨制备Cu-Cr纳米晶粉末[J];粉末冶金材料科学与工程;2013年04期

7 王苗;杨延清;罗贤;;超细晶钛合金的制备及性能研究现状[J];材料导报;2013年13期

8 于影霞;何柏林;;镁合金焊接接头表面自纳米化及其疲劳性能研究现状与展望[J];材料导报;2013年17期

9 吴远志;严红革;朱素琴;陈吉华;刘安民;刘先兰;;Mg-Zn-Zr合金高应变速率多向锻造组织演变及力学性能[J];材料研究学报;2014年02期

10 刘晓燕;赵西成;杨西荣;张凯;解晨;;应变速率对室温下90°等通道转角挤压变形工业纯钛拉伸性能的影响[J];机械工程材料;2013年08期

相关会议论文 前2条

1 于振涛;麻西群;余森;张明华;韩建业;刘春潮;;生物医用钛合金的微纳化加工技术及最新进展[A];第十四届全国钛及钛合金学术交流会论文集（下册）[C];2010年

2 Zhen Zhang;Manping Liu;Yingda Yu;P，

本文编号：2130135