焊后热处理对复杂结构件完整性的影响

发布时间：2018-08-12 11:38

【摘要】：通过考虑热处理前后δCTOD值和残余应力变化,研究了焊后热处理对复杂结构件完整性的影响.对厚板(80 mm)对接接头进行了焊态和热处理态的残余应力测量和断裂韧性(CTOD)试验.相对厚板对接接头焊态,热处理态的残余应力有效降低,焊缝δCTOD值基本不变,热影响区δCTOD值有较大幅度下降;对带拘束和装配应力复杂焊接结构进行局部热处理并测试焊态和热处理态的残余应力.结果表明,残余应力降低不明显,有的部位残余应力水平反而上升.基于以上试验结果,对多种情况进行结构完整性的评估,发现了局部热处理并不能够改善复杂结构的安全性.
[Abstract]:The influence of post-weld heat treatment on the integrity of complex structural parts was studied by considering the variation of delta CTOD value and residual stress before and after heat treatment. The Delta CTOD value of weld seam is basically unchanged, and the delta CTOD value of heat affected zone decreases greatly; the residual stresses of welded structures with complex restraint and assembly stresses are measured by local heat treatment and welding and heat treatment. The results show that the residual stresses are not decreased obviously, but the residual stresses in some parts are increased. It is found that local heat treatment can not improve the safety of complex structures.
【作者单位】：天津大学材料科学与工程学院;
【基金】：国家自然科学基金资助项目(51305295) 教育部博士点新教师基金(20130032120006)
【分类号】：TG441.8

【参考文献】

相关会议论文前10条

1 汪建华;陆皓;;局部焊后热处理加热宽度的直接评定方法[A];第九次全国焊接会议论文集（第2册）[C];1999年

2 汪建华;陆皓;村川英一;;基于粘弹塑性理论局部焊后热处理评定准则研究[A];第五届全国压力容器学术会议论文集[C];2001年

3 蔡洪能;余学瑞;;压力容器焊后热处理工艺优化[A];第四届数控机床与自动化技术高层论坛论文集[C];2013年

4 褚巧玲;李继红;张兴璇;范文静;吴伟刚;张敏;;大型透平机壳焊后热处理数值模拟[A];第四届数控机床与自动化技术高层论坛论文集[C];2013年

5 陆皓;汪建华;村川英一;;Cr-Mo钢管子局部焊后热处理加热宽度准则的确定[A];第十一次全国焊接会议论文集（第2册）[C];2005年

6 张军森;;局部焊后热处理加热宽度的经验确定方法[A];2013年4月现代教育教学探索学术交流会论文集[C];2013年

7 杜随更;时渭清;段立宇;鄢君辉;;GH2132-42CrMo摩擦焊接头焊后热处理行为及使用寿命分析[A];中国电子学会焊接专业青年委员会第一届学术会议论文集[C];1994年

8 张西民;;氢系统2.25 Cr—1 Mo钢的焊后热处理控制[A];中国工程建设焊接协会第八届年会论文集[C];2001年

9 朱瑞灿;张益坤;谢美蓉;程云君;赵刚;;焊后热处理温度对Ti-22A1-25Nb合金电子束焊接接头组织和性能影响研究[A];2008年全国荷电粒子源、粒子束学术会议暨中国电工技术学会第十二届电子束离子束学术年会、中国电子学会焊接专业委员会第九届全国电子束焊接学术交流会、粒子加速器学会第十一届全国离子源学术交流会、中国机械工程学会焊接分会2008年全国高能束加工技术研讨会、北京电机工程学会第十届粒子加速器学术交流会论文集[C];2008年

10 贺新民;;鄂州回转窑简体的焊接[A];中国钢结构协会钢结构焊接分会成立二十周年大会论文集[C];2007年