斜撑离合器楔块线切割工艺优化及变质层分析

发布时间：2018-08-26 16:58

【摘要】：对目前国内PCE型斜撑离合器楔块制造工艺进行概述。为制造高质量的斜撑离合器楔块,提出了一种以慢走丝线切割为核心的楔块加工工艺,采用正交方法对线切割电参数进行了匹配实验,采用扫描电镜对线切割试样表面进行分析。实验结果表明,影响线切割表面粗糙度的因素顺序为脉宽、休止时间、伺服倍率、起始电压,线切割表面存在结构疏松、含Cu和Zn元素、厚度约为15~20μm的变质层。
[Abstract]:The manufacturing process of PCE type oblique clutch wedge in China is summarized. In order to manufacture high quality wedges of oblique brace clutch, a new technology of wedge machining with slow wire cutting as the core is proposed. The electrical parameters of wire cutting are matched by orthogonal method. The surface of wire-cut sample was analyzed by scanning electron microscope (SEM). The experimental results show that the factors affecting the surface roughness of WEDM are pulse width, repose time, servo rate, starting voltage, loose structure on the surface of WEDM, containing elements of Cu and Zn, and a metamorphic layer about 1520 渭 m thick.
【作者单位】： 中南大学机电工程学院;
【基金】：湖南省创新平台与人才计划项目(2015JC3007) 国家重点基础研究项目(2011CB706800-G) 教育部博士点基金项目(20120162110004)
【分类号】：TG48

【相似文献】

相关期刊论文 前10条

1 李建明;靳九成;李学谦;夏宗禹;;大型铁路轴承表面变质层研究[J];湖南大学学报;1989年03期

2 郭涛;王笃诚;;关于电火花线切割变质层的研究[J];电子工艺技术;1991年02期

3 仰书介;磨削变质层状态在线监视仪[J];轴承;1992年03期

4 李崇豪，，赵向东;陶瓷材料电加工后变质层厚度的研究[J];江苏理工大学学报;1996年04期

5 马伏波;陈树峰;;已加工表面变质层的研究[J];煤矿机械;2013年06期

6 殷玲,刘忠,陈日曜;大理石抛光表面变质层的研究[J];磨料磨具与磨削;1993年02期

7 田欣利,徐燕申,彭泽民,林彬;陶瓷磨削表面变质层的产生机理[J];机械工程学报;2000年11期

8 田欣利,林允森,张纾,时小军;高温结构陶瓷精密磨削塑性变质层的物理模型[J];装甲兵工程学院学报;2002年01期

9 林述温,曹瑞涛,莫开旺;轴承沟道磨削变质层与磨削工艺参数关系的研究[J];机械工艺师;1997年01期

10 林述温,莫开旺;轴承沟道磨削工艺参数对磨削变质层的影响规律[J];磨床与磨削;1997年01期

相关会议论文 前2条

1 郑富强;邹丹;臧海天;;硬质合金线切割加工变质层的形成及对材料性能的影响[A];2009全国粉末冶金学术会议论文集[C];2009年

2 张小亮;王兆希;施惠基;;电火花成型对试样表面微观力学性能的影响[A];第16届全国疲劳与断裂学术会议会议程序册[C];2012年

相关硕士学位论文 前2条

1 杨永衡;淬硬模具钢已加工表面变质层的研究[D];哈尔滨理工大学;2015年

2 王静;Cr12MoV线切割电参数优化及变质层研究[D];华中科技大学;2012年

本文编号：2205565