含Nb-Ti低碳微合金钢中纳米碳化物的相间析出行为
[Abstract]:The influence of isothermal temperature on microstructure, properties and precipitation behavior of Nb-Ti microalloyed steel was studied by means of thermal expansion experiment. The precipitation behavior of samples after isothermal temperature was observed and analyzed by TEM. The results show that the precipitated carbides between phases can be observed in the samples at different temperatures, and the surface spacing of the precipitated carbides between phases can be significantly refined by decreasing the isothermal temperature. The interphase precipitation of carbide in the plane and the size of the precipitated carbides between phases. The surface of interphase precipitated carbides with stratified distribution is curved and flat, in which the plane of flat phase precipitates is parallel to the {011}, {012}, {013} and {035} faces of ferrite. The crystal structure of interphase precipitated carbides is determined by HRTEM, the lattice constant is 0.434 nm, and the relationship with ferrite matrix is Baker-Nutting (B-N). By EDS analysis, the precipitated carbides are (Nb,Ti) C. The precipitation strengthening amount is estimated by Orowan mechanism. The results show that the precipitation strengthening amount is more than 300 MPa. at different isothermal temperature.
【作者单位】： 东北大学轧制技术及连轧自动化国家重点实验室;
【基金】：国家自然科学基金资助项目51234002~~
【分类号】：TG142.33
【参考文献】
相关期刊论文 前1条
1 陈俊;吕梦阳;唐帅;刘振宇;王国栋;;V-Ti微合金钢的组织性能及相间析出行为[J];金属学报;2014年05期
【共引文献】
相关期刊论文 前10条
1 庞兆夫,赵小平,温兰伶;10TiZL带钢同卷性能差金相组织分析[J];鞍钢技术;1987年05期
2 陈海林;曾燕屏;李友国;周凡;;含铜无取向电工钢中析出相及其析出机理[J];北京科技大学学报;2011年03期
3 ;Effect of cooling parameters on the microstructure and properties of Mo-bearing and Cr-bearing steels[J];International Journal of Minerals Metallurgy and Materials;2011年05期
4 李艳梅;段争涛;朱伏先;张慧云;;变形和硼对低碳Mn-Nb钢连续冷却转变的影响[J];东北大学学报(自然科学版);2011年10期
5 段争涛;李艳梅;朱伏先;樊中免;;不同工艺低碳Nb-B贝氏体钢组织性能[J];东北大学学报(自然科学版);2012年06期
6 霍向东,柳得橹,孙贤文,康永林,傅杰,王中丙,李烈军,陈贵江;CSP层流冷却工艺对低碳钢组织和性能的影响*[J];钢铁;2003年08期
7 Xiao-pei Wang;Ai-min Zhao;Zheng-zhi Zhao;Yao Huang;Liang Li;Qing He;;Mechanical properties and characteristics of nanometer-sized precipitates in hot-rolled low-carbon ferritic steel[J];International Journal of Minerals Metallurgy and Materials;2014年03期
8 贾涛;魏娇;冯洁;张维娜;刘振宇;王国栋;;低碳钛、钒微合金钢中的相间析出[J];中国工程科学;2014年01期
9 宋峰雨;张朋彦;王平;朱伏先;;板条贝氏体中少量铁素体对高强钢强韧性的影响[J];东北大学学报(自然科学版);2014年05期
10 Jing-jing Yang;Run Wu;Wen Liang;Meng-xia Tang;;Effect of nano-sized precipitates on the crystallography of ferrite in high-strength strip steel[J];International Journal of Minerals Metallurgy and Materials;2014年05期
相关会议论文 前1条
1 常丽杰;董天顺;刘金海;李国禄;陈一帆;范艳林;张建军;;微米晶变质剂对低合金钢组织和性能的影响[A];2014中国铸造活动周论文集[C];2014年
相关博士学位论文 前10条
1 肖福仁;针状铁素体管线钢的组织控制与细化工艺研究[D];燕山大学;2003年
2 余式昌;微合金化奥氏体气阀钢的组织和性能研究[D];东南大学;2006年
3 王磊;高强度桥梁用宽厚板的研制[D];东北大学;2008年
4 吴红艳;低成本超细晶耐候钢的开发研究[D];东北大学;2008年
5 韩峗;低碳马氏体钢中（Ti，Mo）C析出行为及其强韧性研究[D];钢铁研究总院;2013年
6 由园;C-N(-La)共渗层原子间作用第一原理计算与N扩散分子动力学模拟[D];哈尔滨工业大学;2013年
7 冯锐;铁素体/珠光体型钢板内部质量及其影响因素研究[D];山东大学;2013年
8 杨庚蔚;新型超高强度马氏体钢组织超细化控制技术及机理研究[D];昆明理工大学;2013年
9 陈宏涛;奥氏体不锈钢低温稀土氮碳共渗层相结构及其性质研究[D];哈尔滨工业大学;2014年
10 李贞顺;Q690钢板焊接热影响区的组织特征及热稳定性研究[D];山东大学;2014年
相关硕士学位论文 前10条
1 于建国;热变形对高压输气管线钢动态连续冷却转变的影响[D];燕山大学;2011年
2 高飞;V、N微合金化低碳贝氏体钢的成分设计与组织特征[D];昆明理工大学;2011年
3 李鸿美;超低碳中厚板高强高韧化机理研究[D];昆明理工大学;2011年
4 高卫东;抱轴承箱材料ZG25Mn的强韧化研究[D];西南交通大学;2006年
5 杨涛;低碳贝氏体型钢变形奥氏体连续冷却研究[D];上海交通大学;2007年
6 范跃华;高强度管线钢的连续冷却转变研究[D];南京理工大学;2007年
7 王东;钛微合金化钢中钛与非金属元素相互作用基础研究[D];昆明理工大学;2013年
8 王珍传;Ti\Mo微合金化板条马氏体钢析出、组织及力学性能研究[D];昆明理工大学;2013年
9 李小敏;Q345EL大H型钢淬透性的研究[D];山东大学;2014年
10 王东梅;低碳贝氏体钢中温转变机制及组织性能研究[D];东北大学;2011年
【二级参考文献】
相关期刊论文 前1条
1 陈俊;唐帅;刘振宇;王国栋;;冷却方式对Nb-Ti微合金钢组织和性能及沉淀行为的影响[J];金属学报;2012年04期
【相似文献】
相关期刊论文 前10条
1 贾涛;魏娇;冯洁;张维娜;刘振宇;王国栋;;低碳钛、钒微合金钢中的相间析出[J];中国工程科学;2014年01期
2 徐曼,孙新军,刘清友,董瀚,雍岐龙,黄金亮;低碳含钒钢组织变化及V(C,N)析出规律[J];钢铁钒钛;2005年02期
3 陈俊;吕梦阳;唐帅;刘振宇;王国栋;;V-Ti微合金钢的组织性能及相间析出行为[J];金属学报;2014年05期
4 ;[J];;年期
5 ;[J];;年期
6 ;[J];;年期
7 ;[J];;年期
8 ;[J];;年期
9 ;[J];;年期
10 ;[J];;年期
，本文编号：2237466
本文链接：https://www.wllwen.com/kejilunwen/jinshugongy/2237466.html