GCr15轴承钢消除大块状碳化物的热处理工艺

发布时间：2018-10-21 16:58

【摘要】：运用X射线测定了GCr15轴承钢连铸坯芯部宏观偏析区域和微观偏析区域C、Cr元素的浓度。基于C和Cr元素成分分布,用Thermo-Calc软件计算了GCr15轴承钢不同部位的熔点,从而确定了轴承钢连铸坯均匀化加热的最高温度限制。研究了不同温度下消除连铸坯芯部大块状碳化物所需要的时间。通过理论与实验相结合的方法,提出了一系列消除轴承钢连铸坯芯部大块状碳化物的热处理制度。
[Abstract]:The concentration of Cr in the macro segregation region and micro segregation region of GCr15 bearing steel has been determined by X-ray. Based on the composition distribution of C and Cr elements, the melting points of different parts of GCr15 bearing steel were calculated by Thermo-Calc software, and the maximum temperature limit for homogenizing heating of bearing steel continuous casting billet was determined. The time required to eliminate large block carbides in continuous casting billet core at different temperatures was studied. By combining theory with experiment, a series of heat treatment systems for eliminating large block carbides in continuous casting billet of bearing steel have been put forward.
【作者单位】： 北京科技大学热能工程系;北京科技大学新材料技术研究院;
【基金】：国家自然科学基金(51276015)
【分类号】：TG142.1;TG161

【相似文献】

相关期刊论文 前7条

1 刘晓龙;石伟;;中空钢锭芯部压缩空气冷却能力的数值模拟[J];大型铸锻件;2007年06期

2 黄永建;刘才;李会林;;影响棒材轧制芯部质量的因素[J];中国钢铁业;2009年05期

3 黄永建;刘才;李会林;;石钢大规格棒材芯部质量的控制[J];河北冶金;2009年05期

4 贾志雄;;异型材芯部冷却挤出模头设计[J];模具工业;2012年03期

5 李波;陈方玉;;42CrMoS4钢淬火劈裂原因分析[J];钢铁研究;2014年04期

6 张金利;;冷床上钢坯冷却的数值模拟[J];冶金设备;2013年S2期

7 ;[J];;年期

相关会议论文 前1条

1 徐贵娥;李兆霞;方峰;蒋建清;;拉丝失效的研究进展[A];塑性力学新进展——2011年全国塑性力学会议论文集[C];2011年

相关硕士学位论文 前1条

1 刘永;大尺度圆钢热轧成型缺陷控制数值模拟研究[D];燕山大学;2012年

，

本文编号：2285768