Al-Zn-Mg-Cu合金淬透性研究进展
发布时间：2019-01-28 09:14
【摘要】：Al-Zn-Mg-Cu合金密度小,比强度高,具有良好的加工性能,是现代航空航天武器装备等领域发展的关键结构材料。但是对于大型结构件,该系铝合金表现出一定的淬火敏感性。综述了Al-Zn-Mg-Cu合金淬透性研究方法和影响该系铝合金淬透性的因素。其中淬透性研究方法包括:端淬-硬度试验法测定铝合金淬透层深度、TTP曲线、CCT曲线、TTT曲线、理论计算法以及计算机数值模拟法。并且从合金的化学成分、轧制制度、均匀化制度、淬火制度、时效制度和几何尺寸等方面分析了影响淬透性的因素。
[Abstract]:Al-Zn-Mg-Cu alloys with low density, high specific strength and good processing properties are the key structural materials for the development of modern aerospace weapons and equipment. However, for large structural parts, the aluminum alloy shows a certain quenching sensitivity. The research methods of hardenability of Al-Zn-Mg-Cu alloy and the factors affecting the hardenability of the alloy are reviewed. The research methods of hardenability include the depth of quenched layer, TTP curve, CCT curve, TTT curve, theoretical calculation method and computer numerical simulation method. The factors affecting hardenability were analyzed from the aspects of chemical composition, rolling schedule, homogenization system, quenching system, aging system and geometric size of the alloy.
【作者单位】： 长沙理工大学汽车与机械工程学院;长沙理工大学工程车辆轻量化与可靠性技术重点实验室;
【基金】：湖南省自然科学基金(12JJ2023)
【分类号】：TG146.21
[Abstract]:Al-Zn-Mg-Cu alloys with low density, high specific strength and good processing properties are the key structural materials for the development of modern aerospace weapons and equipment. However, for large structural parts, the aluminum alloy shows a certain quenching sensitivity. The research methods of hardenability of Al-Zn-Mg-Cu alloy and the factors affecting the hardenability of the alloy are reviewed. The research methods of hardenability include the depth of quenched layer, TTP curve, CCT curve, TTT curve, theoretical calculation method and computer numerical simulation method. The factors affecting hardenability were analyzed from the aspects of chemical composition, rolling schedule, homogenization system, quenching system, aging system and geometric size of the alloy.
【作者单位】： 长沙理工大学汽车与机械工程学院;长沙理工大学工程车辆轻量化与可靠性技术重点实验室;
【基金】：湖南省自然科学基金(12JJ2023)
【分类号】：TG146.21
【参考文献】
相关期刊论文 前10条
1 刘胜胆;张新明;黄振宝;;淬火速率对7055铝合金组织和力学性能的影响[J];材料科学与工艺;2008年05期
2 赵中魁,周铁涛,刘培英,陈昌麒;Al-Zn-Mg-Cu-Li-Er合金时效组织中Er相的TEM观察[J];稀有金属材料与工程;2004年10期
3 刘胜胆;张新明;游江海;张小艳;;微量锆对7055型铝合金淬火敏感性的影响[J];稀有金属材料与工程;2007年04期
4 陈志国;杨文玲;王诗勇;舒军;;微合金化铝合金的研究进展[J];稀有金属材料与工程;2010年08期
5 李克生 ,田进安;一种新型淬火介质的应用研究[J];国外金属热处理;2004年02期
6 张新明;欧阳惠;刘胜胆;吴泽政;王雷;周志乐;;固溶处理对Al-7.9Zn-2.5Mg-1.0Cu合金淬火敏感性的影响[J];材料研究学报;2013年02期
7 张新明;余翠娟;刘胜胆;刘星兴;张盼;王莹莹;;Fe和Si杂质对Al-Zn-Mg-Cu合金淬火敏感性的影响[J];材料工程;2013年10期
8 刘胜胆;张新明;游江海;张小艳;张，
本文编号：2416924
本文链接：https://www.wllwen.com/kejilunwen/jinshugongy/2416924.html
教材专著