钠在Al-4.5%Cu合金中的存在形式及不利影响（英文）

发布时间：2019-03-21 08:02

【摘要】：通过熔盐向Al-4.5%Cu引入足量的钠,研究钠在Al-Cu合金中的存在形式以及对合金显微组织和抗拉性能的影响。结果表明:钠以单质形式存在于合金晶界中,这种钠降低了基体和CuAl_2相之间的结合力。T6时效处理后,钠导致了微观裂纹的产生和CuAl_2相的残留。抗拉实验的结果显示钠使得合金的断裂方式由韧窝断裂向晶间断裂转变,这导致了合金性能的急剧降低。
[Abstract]:The existence form of sodium in Al-Cu alloy and its effect on microstructure and tensile properties of Al-Cu alloy were studied by introducing sufficient amount of sodium into Al-4.5%Cu by molten salt. The results show that sodium exists in the grain boundary of the alloy in the form of single substance, which reduces the binding force between the matrix and CuAl_2 phase. After aging treatment with T6, sodium leads to the formation of microcracks and the residue of CuAl_2 phase. The results of tensile test show that the fracture mode of the alloy is changed from dimple fracture to intergranular fracture, which leads to a sharp decrease in the properties of the alloy.
【作者单位】： 山东大学材料液固结构演变与加工教育部重点实验室;
【分类号】：TG146.21

【参考文献】

相关期刊论文 前1条

1 孙宝德,丁文江,疏达,周尧和;Purification technology of molten aluminum[J];Journal of Central South University of Technology(English Edition);2004年02期

【相似文献】

相关期刊论文 前10条

1 石德珂,刘军海;高锰钢的断裂特性[J];兵器材料科学与工程;1989年10期

2 阎立珠;气伐钢的新热处理法[J];热加工工艺;1978年06期

3 ;"330"叶片生产技术总结 六、讨论意见[J];大型铸锻件;1980年01期

4 张帆;赵建平;;内聚力单元在Voronoi元胞的晶间断裂模拟中的应用[J];组合机床与自动化加工技术;2013年11期

5 R.J.Acuna;李溪滨;;6063铝合金的断裂行为——化学成分和时效状态的影响[J];轻金属;1985年04期

6 吴波;魏悦广;谭建松;王建平;;纳米晶Ni晶间断裂的数值模拟[J];金属学报;2009年09期

7 H.科迪埃;赵小兵;;可焊A1-Zn-Mg合金的显微组织和晶间断裂[J];国外舰船技术(材料类);1981年02期

8 陈升媛;;微量元素对镍铬铈合金延性和断裂的影响[J];上海金属.有色分册;1988年02期

9 朱彦生;;基于有限元模拟的纳米晶Ni的晶间断裂分析[J];铸造技术;2014年07期

10 齐芸馨，王玉忠，，夏建国，王改莲;电渣熔铸35CrNi3MoV钢枝晶间断裂的俄歇分析[J];钢铁;1996年06期

相关会议论文 前1条

1 刘新权;吴德振;杨恩超;苏化冰;阚继友;;热处理工艺对X20Cr13叶片用钢FATT_(50)和晶间断裂的影响[A];中国动力工程学会透平专业委员会2012年学术研讨会论文集[C];2012年

本文编号：2444743