热处理对TA7合金再结晶程度及力学性能的影响

发布时间：2019-03-29 06:07

【摘要】：研究了TA7合金在不同热处理温度下的再结晶程度对板材力学性能的影响。结果表明:随热处理温度升高,TA7合金板材再结晶程度增强,对应的板材塑性增加,强度略有下降;断口分析表明,随再结晶程度增加,位错聚集区域减少,加工应力释放,断裂区域大部分呈现出细小椭圆或等轴的韧窝,表现出更好的材料塑性。
[Abstract]:The effect of recrystallization degree on the mechanical properties of TA7 alloy at different heat treatment temperatures was studied. The results show that with the increase of heat treatment temperature, the recrystallization degree of TA7 alloy sheet increases, the plasticity of the corresponding plate increases, and the strength decreases slightly. The fracture analysis shows that with the increase of recrystallization, the dislocation aggregation region decreases and the processing stress is released. Most of the fracture areas show fine ellipse or equiaxed dimples, showing better material plasticity.
【作者单位】： 西部钛业有限责任公司;
【分类号】：TG166.5;TG146.23

【相似文献】

相关期刊论文 前10条

1 卫平,李嘉荣,钟振纲;一种镍基单晶高温合金的表面再结晶研究[J];材料工程;2001年10期

2 王林山,陈康华,刘红卫,熊翔,刘允中;强化处理和快速再结晶对2014铝合金组织与性能的影响[J];有色金属;2001年01期

3 何彪;李运菊;张卫方;鲁玉祥;;表面再结晶对定向凝固高温合金高周疲劳行为的影响[J];航空材料学报;2007年02期

4 王志刚;赵京晨;燕平;周铁涛;刘培英;;一种镍基单晶高温合金的再结晶[J];钢铁研究学报;2009年02期

5 撒世勇;谢光;;涂层对定向凝固高温合金表面再结晶的影响研究[J];表面技术;2009年01期

6 池田千里;池田圭介;田中英八郎;杨德春;;铝热挤压材表面粗大再结晶层的原因[J];轻合金加工技术;1981年05期

7 陈康华;陈送义;彭国胜;方华婵;肖代红;;变形程度对7150铝合金再结晶及性能的影响[J];特种铸造及有色合金;2010年02期

8 华琪;邵光杰;;Si元素对变形铝合金再结晶影响[J];材料热处理学报;2012年01期

9 刘文辉;王猛;李茂华;;再结晶后面心立方金属的断裂模式及有限元分析[J];机械工程材料;2010年05期

10 徐石斌;王贤民;;GH220合金工艺塑性与再结晶研究[J];航空材料;1983年01期

相关会议论文 前3条

1 贾大炜;施惠基;;表面再结晶 DZ4材料高温低周疲劳性能分析[A];第九届全国热疲劳学术会议论文集[C];2007年

2 贾波;李运菊;;表面再结晶对DZ4合金高温低周疲劳性能的影响[A];2007年全国失效分析学术会议论文集[C];2007年

3 张传臣;张田仓;季亚娟;黄继华;;摩擦压力对异质钛合金线性摩擦接头焊界面组织的影响[A];第十六次全国焊接学术会议论文摘要集[C];2011年

相关硕士学位论文 前3条

1 宋畅;CSP再结晶模型及其组织与性能研究[D];武汉科技大学;2011年

2 魏延;铌对B220P2汽车用冷轧板组织及性能的影响[D];内蒙古科技大学;2015年

3 朱大鹏;微量钪和锆对Al-Mg-Mn合金组织性能的影响[D];中南大学;2004年

，

本文编号：2449223