镍铝青铜化学镀镍磷合金和性能

发布时间：2019-04-04 13:33

【摘要】：以船用铜合金镍铝青铜为基体,采用酸性化学镀溶液体系制备镍磷合金镀层,对该镍磷镀层的界面结合情况及其强度、表面形貌、化学成分组成、硬度、耐海水腐蚀性能等进行了研究。结果显示,镀层为高磷非晶镀层,组织均匀致密,无孔隙等明显缺陷,界面结合强度高,同时硬度较高(646 HV),耐海水腐蚀性能明显优化。可见采用化学镀镍磷合金对镍铝青铜进行表面改性处理,可有效提高其综合性能,保护基体材料,延长其在海水中的服役寿命。
[Abstract]:Ni-P alloy coating was prepared by acid electroless plating solution with copper alloy Ni-Al bronze as substrate. The interface bonding, strength, surface morphology, chemical composition and hardness of Ni-P coating were studied. The corrosion resistance of seawater was studied. The results show that the coating is a high-phosphorus amorphous coating with uniform and dense microstructure, no obvious defects such as pores, high interfacial bonding strength and high hardness (646 HV), and the corrosion resistance of seawater is obviously optimized. It can be seen that the surface modification of Ni-Al bronze by electroless plating Ni-P alloy can effectively improve its comprehensive properties, protect the matrix material and prolong its service life in seawater.
【作者单位】： 江苏大学先进制造与现代装备技术工程研究院;
【基金】：江苏大学优秀学术青年骨干培养对象基金资助项目(1211110001) 校企产学研合作项目(1801110288)
【分类号】：TG174.4

【相似文献】

相关期刊论文 前10条

1 徐健,邢建东,李镜银;镍铝青铜的熔铸工艺特点[J];材料开发与应用;2004年02期

2 宋德军;胡光远;卢海;胡伟民;;镍铝青铜合金的应用与研究现状[J];材料导报;2007年S3期

3 张晓菲;彭成章;肖阳;朱金水;;镍铝青铜高温变形的本构模型研究[J];热加工工艺;2012年20期

4 孙扬善;;镍铝青铜的回火组织[J];金属热处理;1990年01期

5 史鑫;宋德军;胡伟民;;新型镍铝青铜合金组织研究[J];热加工工艺;2009年10期

6 张晓菲;彭成章;肖阳;朱金水;;退火对镍铝青铜合金组织和性能的影响[J];热加工工艺;2012年18期

7 G、M、文斯顿;汤文新;;海洋环境用镍铝青铜铸造合金的综述[J];国外舰船技术(材料类);1985年04期

8 ;18%Cr系不锈铸钢在海水中的耐浸蚀性[J];特钢技术;1994年03期

9 许晓静;陈树东;潘励;魏建;侍国防;;锆微合金化铸态镍铝青铜的组织与性能[J];稀有金属;2014年01期

10 许晓静;陈树东;楚满军;潘励;魏建;侍国防;;钪、锆和锶复合微合金化铸态镍铝青铜的显微组织与性能[J];中国有色金属学报;2013年12期

相关硕士学位论文 前2条

1 都春燕;镍铝青铜合金的耐蚀性及表面处理的研究[D];江苏科技大学;2014年

2 刘利涛;镍铝青铜构件的最优化补焊方法及其物相的快速EDS相分析[D];天津大学;2012年

，

本文编号：2453864