25CrMo钢端淬试验改进与淬透性分析

发布时间：2019-04-12 15:43

【摘要】：为了克服常规端淬试验中25Cr Mo钢试样在空气中发生淬火现象,提出了一种改进的加套管的末端淬火试验方法。通过显微组织观察、定量金相和硬度测量,分析了25Cr Mo钢的显微组织与淬透性。结果表明,改进的端淬试验能够使热量沿轴向传递,避免了产生边角效应。端淬后的试样由水冷端向空冷端的显微组织依次为马氏体、马氏体+贝氏体、贝氏体。25Cr Mo钢淬硬层深度可达20 mm,具有良好的淬透性。
[Abstract]:In order to overcome the quenching phenomenon of 25Cr Mo steel specimen in air during conventional end quenching test, an improved end quenching test method of casing was proposed. The microstructure and hardenability of 25Cr Mo steel were analyzed by means of microstructure observation, quantitative metallography and hardness measurement. The results show that the improved end quenching test can make the heat transfer along the axial direction and avoid the side angle effect. The microstructure of the quenched sample from water-cooled end to air-cooled end is martensite, martensite bainite and bainite. The hardened layer depth of 25Cr Mo steel can reach 20 mm, and has good hardenability.
【作者单位】： 沈阳理工大学材料科学与工程学院;中国科学院金属研究所;
【基金】：科技部支撑计划(No.2009BAG 12A07-C02-1)
【分类号】：TG142.1

【参考文献】

相关期刊论文 前5条

1 刘曙蓉,佘毅云;电力机车车轴热处理工艺的研究[J];电力机车与城轨车辆;2005年06期

2 刘庚武;;EA4T材料的锻造与热处理工艺研究[J];锻压技术;2010年01期

3 张熹;王春旭;刘宪民;史庆南;;化学成分波动对SAE9310钢淬透性和力学性能的影响[J];钢铁;2007年05期

4 梁益龙;王新;孟阳;王筑生;张春红;;国产EA4T车轴钢的显微组织与强韧性研究[J];热加工工艺;2008年16期

5 吴立新;陈士华;彭志方;;电力机车车轴断裂分析[J];物理测试;2009年04期

【共引文献】

相关期刊论文 前10条

1 张建华;梁益龙;王伟韬;;EA4T钢冷却过程中脉冲电流对组织与性能的影响[J];兵器材料科学与工程;2011年03期

2 施耀新;田洪志;;反应堆压力容器母材60年寿命性能要求及工艺措施[J];发电设备;2012年02期

3 厉勇;王春旭;刘宪民;田志凌;许广鹏;赵肃武;;SAE9310钢奥氏体的冷却转变行为[J];机械工程材料;2010年05期

4 李亚宁;梁晨;覃作祥;陆兴;;两种低碳铬钼钢的等温淬火组织和性能[J];大连交通大学学报;2013年01期

5 杨延辉;王毛球;陈敬超;董瀚;;齿轮钢高温渗碳后的疲劳性能[J];钢铁;2013年07期

6 于鑫;李世涛;孙杰;;EA4T车轴车削表面完整性研究[J];工具技术;2014年09期

7 于鑫;孙杰;李世涛;李剑峰;;滚压工艺对EA4T车轴表面质量完整性的影响及预测模型建立[J];中国表面工程;2014年05期

8 田伟;李红斌;徐树成;郑明月;;25CrMo钢的热变形行为及加工图[J];兵器材料科学与工程;2014年06期

9 雷e，

本文编号：2457142