Microstructure Stability of V and Ta Microalloyed 12%Cr Redu

发布时间：2020-12-20 02:55

　　In view of developing novel alloys for applications in supercritical water-cooled reactor fuel cladding and in-core components, a 12%Cr reduced activation ferrite/martensite（RAFM） steel with good corrosion resistance and irradiation performance was developed. V and Ta were added to form fine MX type carbonitrides and enhance the high temperature creep rupture strength. Microstructure stability of the steel during long-term aging at 650 C was studied experimentally combined with the simulation of... 