【摘要】：裂纹的扩展行为研究是压力容器剩余寿命预测的关键与基础。针对目前难以准确预测压力容器表面裂纹剩余寿命的状况,通过建立压力容器表面裂纹的受力模型,利用有限元方法分别计算出裂纹表面点与最深点处的应力强度因子,得到裂纹深度a与长度c的变化之比,运用压力容器仿真系统进行路径仿真与失效速率仿真,得到裂纹在安全区域的临界拐点及临界值aN。实例计算结果表明,表面裂纹的失效路径能够直观准确的表示裂纹的扩展规律,进行有效的剩余寿命预测。
[Abstract]:Study on the crack propagation behavior is the key and foundation of the residual life prediction of pressure vessel. Aiming at the difficulty in accurately predicting the residual life of pressure vessel crack surface condition, through the stress model of surface cracks in pressure vessel, finite element method is used to calculate the crack surface and the deepest point of the stress intensity factor of crack is obtained the depth change of a and the ratio of the length of C, using the simulation system of pressure vessel path simulation simulation and failure rate, the cracks were calculated in the aN. instance of critical security zone inflection point and critical value. The results show that the failure path of surface crack can accurately express the crack propagation, for residual life prediction effectively.

【作者单位】：四川大学制造科学与工程学院;
【基金】：国家自然科学基金项目(51075286)资助
【分类号】：TH49;TG115
【正文快照】： 压力容器的剩余寿命由裂纹的形成寿命与扩展寿命两部分组成,裂纹的扩展主要包括微裂纹扩展与宏观裂纹扩展,通常,在工程应用中都避免使用含有宏观裂纹的压力容器[1]。不过,由于材料本身含有一些微缺陷,在高温、高压、腐蚀等环境以及应力集中、加载频率、应力比等因素的影响下,

【相似文献】