【摘要】：延性金属动态拉伸破坏(层裂)是跨空间尺度、跨时间、跨结构层次的多尺度耦合现象,是不可逆的、远离平衡的非线性演化过程,如何联系微观尺度上的损伤机制理解和宏观尺度上的破坏行为预测是当下学术界面临的挑战.本文结合课题组之前的工作,对延性金属动态拉伸断裂的宏观响应、损伤演化机理和物理模型构建的研究进展和现状进行了评述,从多个时空尺度对延性金属动态拉伸断裂进行全面介绍,并分析了延性金属动态拉伸断裂的跨尺度演化研究所面临的困难和挑战.
[Abstract]:Dynamic tensile failure (spallation) of ductile metals is a multi-scale coupling phenomenon across spatial scale, time and structure level, which is irreversible and far from equilibrium nonlinear evolution process. How to understand the damage mechanism at the micro scale and predict the damage behavior at the macro scale is a challenge facing the academic community. This paper combines the previous work of the research group to study the macroscopic response to the dynamic tensile fracture of ductile metals. The research progress and present situation of damage evolution mechanism and physical model construction are reviewed, and the dynamic tensile fracture of ductile metals is comprehensively introduced from several space-time scales. The difficulties and challenges in the cross-scale evolution of ductile metal dynamic tensile fracture are analyzed.
【作者单位】： 中国工程物理研究院流体物理研究所冲击波物理与爆轰物理重点实验室;武汉理工大学理学院;阿贡国家实验室先进光子源;
【基金】：国家自然科学基金(编号:11302202,11532012) 国家自然科学基金委员会与中国工程物理研究院联合基金(编号:U1330111) 中国工程物理研究院院长基金(编号:201402084) 冲击波物理与爆轰物理重点实验室基金(编号:9140C670301150C67290)资助项目
【分类号】：O346.1

【相似文献】

相关期刊论文 前8条

1 贺红亮;;动态拉伸断裂的物理判据研究[J];高压物理学报;2013年02期

2 张哲峰;新的统一拉伸断裂准则——椭圆准则[J];中国基础科学;2005年03期

3 林红;陈国明;陈养厚;;含裂纹金属拉伸断裂过程的热像检测方法[J];中国石油大学学报(自然科学版);2008年05期

4 王永刚;贺红亮;;20~#钢动态拉伸断裂行为及其临界损伤度研究[J];固体力学学报;2008年04期

5 王永刚;贺红亮;王礼立;经福谦;;延性材料动态拉伸断裂早期连通过程的逾渗描述[J];高压物理学报;2006年02期

6 刘磊;刘亚东;张亚军;徐胜利;;含不同角度穿透裂纹板拉伸断裂的有限元模拟[J];中国科学技术大学学报;2012年04期

7 刘亚东;张亚军;徐胜利;;含垂直穿透裂纹板拉伸断裂的有限元模拟[J];中国科学技术大学学报;2010年03期

8 ;[J];;年期

相关会议论文 前1条

1 贺红亮;;延性金属动态拉伸断裂的损伤演化[A];中国力学学会学术大会'2009论文摘要集[C];2009年

相关博士学位论文 前1条

1 王永刚;延性金属动态拉伸断裂及其临界损伤度研究[D];中国工程物理研究院;2006年

，

本文编号：1685455