超声波功率对激光熔覆铁基汽车制动耐磨涂层组织与性能的影响

发布时间：2018-05-17 10:29

  本文选题：刹车片 + 激光熔覆　； 参考：《热加工工艺》2016年14期

【摘要】：采用激光熔覆方法在Q235钢基体表面制备一种高强度、高硬度和高耐磨性的涂层。同时借助光学显微镜、洛氏硬度计和磨粒磨损试验机等手段,研究超声波功率对涂层组织与性能的影响。结果表明:超声波功率对涂层组织与性能影响显著。随超声波功率的增大,在空化效应以及声流作用下,涂层显微组织逐渐细化。涂层硬度与相对耐磨性都呈先增加后减小的变化规律。当超声波功率增大到1000 W时,涂层组织非常细小,硬度达到最大值62 HRC,相对耐磨性达到最大值,其耐磨性是基体的24倍左右。
[Abstract]:A kind of coating with high strength, high hardness and high wear resistance was prepared on Q235 steel substrate by laser cladding. The influence of ultrasonic power on the microstructure and properties of the coating was studied by means of optical microscope, Rockwell hardness tester and abrasive wear tester. The results show that ultrasonic power has a significant effect on the microstructure and properties of the coating. With the increase of ultrasonic power, the microstructure of the coating is gradually refined under the effect of cavitation and acoustic flow. The hardness and relative wear resistance of the coating increased first and then decreased. When the ultrasonic power is increased to 1000 W, the microstructure of the coating is very fine, the hardness reaches the maximum value of 62 HRC, the relative wear resistance reaches the maximum, and the wear resistance of the coating is about 24 times that of the substrate.
【作者单位】： 湖南汽车工程职业学院;江西昌河铃木汽车有限公司;
【分类号】：U463.5;TG174.4

【相似文献】

相关期刊论文 前6条

1 李军文;桃野正;付莹;;超声波功率对铸锭内的气孔及组织细化的影响[J];铸造;2007年02期

2 李军文;郭文涛;韩志凡;颜宏;;超声波功率对ZA27合金凝固组织及力学性能的影响[J];热加工工艺;2011年13期

3 林莉,李喜孟,谭家隆,张俊善;超声波功率谱技术无损区分GCr15SiMn钢显微组织的探讨[J];金属热处理学报;2002年04期

4 李杰;陈伟庆;王晓峰;;超声波功率对高碳钢中夹杂物的影响[J];北京科技大学学报;2009年09期

5 李杰;陈伟庆;;超声波熔体处理对高碳钢凝固组织和性能的影响[J];铸造;2008年10期

6 ;[J];;年期

相关会议论文 前1条

1 郭文涛;李军文;贾征;;超声波功率对ZA27合金凝固组织及力学性能的影响[A];2009中国铸造活动周论文集[C];2009年

，

本文编号：1901021