吸附区粉煤灰混凝土抗硫酸盐腐蚀性能研究

发布时间：2018-05-16 10:54

  本文选题：粉煤灰混凝土 + 浸泡区　； 参考：《中国矿业大学学报》2014年04期

【摘要】：采用浸泡、半浸泡的试验方法,定期检测混凝土的超声声速和抗压强度,并观察不同腐蚀期试件的表观现象.结果表明:随着腐蚀时间的增长,试件腐蚀层厚度逐渐增加,腐蚀速率先降低后升高最后趋于稳定;抗压强度先增大后减小,强度损失度逐渐增大;吸附区普通混凝土破坏最严重,浸泡区粉煤灰混凝土破坏最轻微.通过机理分析建立半浸泡混凝土受硫酸盐腐蚀性能的退化模式.
[Abstract]:The ultrasonic velocity and compressive strength of concrete were measured periodically by means of immersion and semi-immersion, and the apparent phenomena of specimens in different corrosion periods were observed. The results show that with the increase of corrosion time, the thickness of corrosion layer increases gradually, the corrosion rate decreases first and then increases and then tends to stabilize, the compressive strength increases first and then decreases, and the strength loss increases gradually. The damage of ordinary concrete in adsorption zone is the most serious, and that of fly ash concrete in soaking area is the least. Through mechanism analysis, a degradation model of sulfate-corrosion behavior of semi-immersed concrete was established.
【作者单位】： 中国矿业大学力学与建筑工程学院江苏省土木工程环境灾变与结构可靠性重点实验室;中国水电顾问集团华东勘测设计研究院有限公司;
【基金】：国家自然科学基金项目(51178455) 国家高技术研究发展计划(863)项目(2012AA06A402)
【分类号】：TU528.2

【相似文献】

相关期刊论文 前10条

1 孙云岳;模拟移动床吸附分离(Ⅱ)——调优运算[J];化学工程;1984年04期

2 王锐清;;一种吸附、解吸同步化工业化设备及反渗透浓缩组合设备的设计[J];现代化工;2007年09期

3 黎树勋;;多柱串联吸附分离过程的工艺设计[J];石油化工;1975年01期

4 孙云岳;模拟移动床吸附分离(Ⅰ)—计算模型[J];化学工程;1984年03期

5 申福生;;低温吸附器的工作时间与吸附效果[J];冶金动力;1991年02期

6 金观涛;乐成秀;朱熹豪;;模拟移动床的数学模型[J];石油化工;1977年01期

7 张金辉;连续离子交换技术在硝酸钾生产中的应用[J];中氮肥;2001年05期

8 王永灵,黄艳丽,唐起祥;变压吸附制氮技术[J];中国氯碱;2003年02期

9 关春梅;分子筛工作周期的改进[J];中氮肥;2004年03期

10 蔡振国;李兆星;孔伟;;离子交换移动床模拟实验装置的建立及其应用测试[J];现代商贸工业;2008年12期

相关会议论文 前1条

1 赵锡武;何玉莲;邵伟;;模拟移动床技术及应用[A];第三届全国工业催化技术及应用年会论文集[C];2006年

，

本文编号：1896553