干湿循环腐蚀环境下钢筋混凝土柱的锈胀裂缝分析

发布时间：2018-03-17 11:37

  本文选题：干湿循环　切入点：腐蚀　出处：《混凝土》2017年06期 　论文类型：期刊论文

【摘要】：通过7组钢筋混凝土墩柱的通电锈蚀及干湿循环试验,研究氯盐侵蚀和干湿循环作用对混凝土墩柱锈胀裂缝形态及分布的影响。试验通过控制通电电流和通电时间得到试件不同的钢筋腐蚀率;通过控制试件浸泡盐溶液的水位高低的周期性变化实现试件的干湿循环作用。试验结果表明:在腐蚀率相近时,干湿循环腐蚀试件相较单一腐蚀试件而言,其锈胀裂缝数量有着明显的增加,试件的最大裂缝宽度至多增加约100%,其平均裂缝宽度则至多增加约83.3%。
[Abstract]:Through the electrical corrosion and dry and wet cycle tests of 7 groups of reinforced concrete pier columns, The effects of chloride erosion and dry and wet cycling on the form and distribution of rust expansion crack of concrete pier column were studied. The corrosion rate of steel bar was obtained by controlling the current and time of electrification. By controlling the periodic variation of the water level of the salt solution, the dry and wet cycle of the specimen is realized. The test results show that when the corrosion rate is similar, the dry and wet cycle corrosion specimen is better than the single corrosion specimen. The maximum crack width of the specimen increases by about 100 at most, and the average crack width increases by about 83.3 percent at most.
【作者单位】： 上海交通大学船舶海洋与建筑工程学院;
【基金】：国家自然科学基金项目(51178264) 铁道部科技研究开发项目(J2011G003)
【分类号】：TV33

【相似文献】

相关期刊论文 前10条

1 何忠意;邓安;周亚东;王海波;;干湿循环下复合固废填料配比对强度的影响[J];建筑材料学报;2011年06期

2 薛文;王卫仑;龚顺风;金伟良;;干湿循环下氯离子在混凝土中的传输[J];低温建筑技术;2010年06期

3 曹光栩;宋二祥;徐明;;碎石料干湿循环变形试验及计算方法[J];哈尔滨工业大学学报;2011年10期

4 袁璞;马芹永;;干湿循环条件下煤矿砂岩分离式霍普金森压杆试验研究[J];岩土力学;2013年09期

5 李克钢;吴勇;郑东普;;砂岩力学特性对干湿循环效应响应规律的试验研究[J];北京理工大学学报;2013年10期

6 张俊然;许强;孙德安;;多次干湿循环后土-水特征曲线的模拟[J];岩土力学;2014年03期

7 张伟勤;刘连新;代大虎;;混凝土在卤水、淡水中的干湿循环腐蚀试验研究[J];青海大学学报(自然科学版);2006年04期

8 李克钢;郑东普;黄维辉;;干湿循环作用下砂岩力学特性及其本构模型的神经网络模拟[J];岩土力学;2013年S2期

9 刘文化;杨庆;唐小微;李吴刚;;干湿循环条件下不同初始干密度土体的力学特性[J];水利学报;2014年03期

10 李固华;高波;;纳米CaCO_3对砼耐干湿循环腐蚀性能的影响[J];重庆交通学院学报;2007年02期

相关会议论文 前6条

1 卫军;余t，

本文编号：1624572