石粉含量对C60机制砂海工混凝土耐久性的影响研究

发布时间：2018-09-03 06:43

【摘要】：研究了花岗岩机制砂石粉含量(5%、7%、10%)对C50机制砂海工混凝土(MSC)耐久性关键参数的影响,并与河砂混凝土(RSC)进行比较。结果表明:当机制砂石粉含量为7%时,混凝土的抗碳化性能、氯离子扩散系数及其龄期衰减系数、抗硫酸盐侵蚀性能、护筋性能等耐久性指标均达到最佳,且优于河砂混凝土;另外,外掺4.5%~15%石粉均改善了胶浆的氯离子结合性能,当石粉掺量为胶材质量的7.5%时,氯离子结合能力最强。
[Abstract]:The effect of granite-machined sand powder content (5%) on the durability of C50 sand marine concrete (MSC) was studied and compared with that of river sand concrete (RSC). The results show that the durability indexes of concrete, such as carbonation resistance, chloride diffusion coefficient and age attenuation coefficient, sulfate corrosion resistance and reinforcement protection performance, are the best when the content of machine-made sand and stone powder is 7, and is better than that of river sand concrete. In addition, the addition of 4.5% stone powder improved the chloride binding properties of the paste. When the content of the stone powder was 7.5% of the mass of the rubber, the binding capacity of the chloride ion was the strongest.
【作者单位】： 武汉理工大学硅酸盐建筑材料国家重点实验室;山东省交通科学研究院;中铁建大桥工程局集团第一工程有限公司;
【基金】：国家自然科学基金资助项目(51372185)
【分类号】：TV431

【相似文献】

相关期刊论文 前10条

1 诸葛志文;;浅谈机制砂在海工砼中的应用技术[J];黑龙江科技信息;2014年15期

2 高怀英;齐连瑞;李广智;袁春波;;机制砂混凝土性能试验研究[J];水科学与工程技术;2009年01期

3 孟繁义;;机制砂在水利工程中的应用若干问题探讨[J];水利建设与管理;2009年07期

4 蔡胜华;杨华全;周浪;柏沁;王晓军;;石粉含量对大坝碾压混凝土性能的影响[J];水力发电;2008年01期

5 田明明;袁丰;彭章毅;;阿海水电站灰岩制砂高石粉含量工艺控制研究[J];云南水力发电;2012年03期

6 王玉珏;孙其龙;;机制沙石粉含量的试验分析[J];黄河水利职业技术学院学报;2008年04期

7 赵铁军,万小梅;一种预测混凝土氯离子扩散系数的方法[J];工业建筑;2001年12期

8 姚昌建;金伟良;王海龙;金立兵;延永东;;海工混凝土氯离子扩散系数随深度的变化规律[J];水利水运工程学报;2008年04期

9 叶铭勋;胡竹魂;;氯离子扩散系数的测定[J];水利水运科学研究;1986年04期

10 黄绪通，韩正江;人工砂石粉含量对混凝土性能影响的研究与应用[J];水力发电;1995年01期

相关会议论文 前2条

1 蔡胜华;陈文卓;张杰;;石粉含量对大坝碾压混凝土性能的影响[A];2012年度碾压混凝土筑坝技术交流研讨会论文集[C];2012年

2 文科;王文涛;;亭子口水利枢纽工程成品砂中石粉含量控制的研究[A];2012年度碾压混凝土筑坝技术交流研讨会论文集[C];2012年

相关博士学位论文 前1条

1 熊建波;荷载与冻融共同作用下氯离子在海工混凝土中扩散行为研究[D];华南理工大学;2016年

相关硕士学位论文 前1条

1 陈培杰;海工水泥混凝土基本性能和氯离子扩散特性的试验研究[D];浙江工业大学;2015年

，

本文编号：2219211