文献名称：PVC与核壳结构聚丙烯酸酯及环氧树脂的共混增韧

    前言：研究发现由分段乳液聚合丙烯酸丁酯、甲基丙烯酸甲酯、甲基丙烯酸缩水甘油酯制备的三层核壳结构共聚体和少量环氧树脂(含固化剂及促进剂)与PVC在适当配比下共混,可使改性PVC的抗冲击性能明显提高。考察了共混体系的组成与其冲击强度及断裂形态之间的关系。
    Core-shell particles for toughening PVC were prepared by sequential emulsion polymerization of butyl acrylate(BA) , methyl methacrylate(MMA) and glycidyl methacrylate (GMA). Blending of these particles and small amounts of epoxy resin, including curing agent and accelerator, together with PVC gives materials with greatly enhanced impact strength at a optimized weight fraction. Dependence of impact strength and fracture morphology of the toughened PVC material upon the variation of blending composition has b...

文献名称 PVC与核壳结构聚丙烯酸酯及环氧树脂的共混增韧

Article Name
英文(英语)翻译 Toughening of PVC via Blending of Core-Shell Polyacrylic-ester Copolymer and Epoxy Resin;

作者 张保龙; 王淑芳; 黄吉甫; 丁培元; 杜宗杰; 宋谋道; 张邦华;

Author ZHANG Bao-Long;WANG Shu-Fang;HUANG Ji-Fu;DING Pel-Yuan;DU Zhong-Jie （Departntent of Chemistry;Nankai University;Tianjin;300071）SONG Mou-Dao;ZHANG Bang-Hua （Institute of Polymer Chemistry;300071）;

作者单位
Author Agencies 南开大学化学系; 南开大学高分子化学研究所; 南开大学高分子化学研究所 天津;

文献出处
Article From 中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度

关键词 核壳结构共聚体; 环氧树脂; PVC; 甲基丙烯酸缩水甘油酯;

Keywords Core-shell copolymer;Epoxy resin;PVC;Glycidyl methacrylate;

新型络合吸附剂的研究(Ⅱ)——铜离子模板高分子多乙烯多胺络合吸附剂的合成和特性
乳液聚合共聚物玻璃化转变温度及其理论计算
TiCl_4/Al_2Et_3Cl_3/Y-型分子筛高效乙烯丙烯共聚催化体系的研究
α-烃基取代吡啶对金(Ⅲ)的萃取研究(Ⅰ)——电离常数的测定和金的萃取行为
MZr_2(AsO_4)_3(M=Na,K,Rb,Cs)的水热合成与结构表征
α-和β-[SiW_9O_(37)M_3(H_2O)_3]~(7-)(M=A1~(3+),Ga~(3+),In~(3+))的合成和钨-183核磁共振研究
铁-磷-硼纳米金属玻璃的化学制备与穆斯堡尔研究
α-烃基取代吡啶对金(Ⅲ)的萃取研究(Ⅱ)
差示脉冲极谱法对镉(Ⅱ)-草酸-琥珀酸混配三元配合物的研究
非配对型电极上的示波沉淀滴定

  本文关键词：张保龙，，由笔耕文化传播整理发布。