铁管装饰电镀工艺及发展

发布时间：2018-03-17 06:02

  本文选题：~+铁基管件电镀　切入点：~+装饰电镀　出处：《航天工艺》1992年04期 　论文类型：期刊论文

【摘要】：铁基管件的装饰电镀的关键在于选择合理的中间镀层及合理的电镀工艺。如选用高氰Cu-Sn合全电镀液,成本低,镀层质量好,但溶液剧毒,磨光、抛光劳动量较大;选用镍、光亮镍作中间层,成本又很高;选用光亮Ni-Fe合金作为中间层,电镀液维护较困难;选用酸性亮铜镀铜,再镀薄镍作为中间镀层,成本低,效果好。在工艺上必须采用辅助阳极、镀软铁、化学浸铜等工序可防止置换铜粉和二价铁污染溶液。无毒碱性光亮镀铜代替酸性光亮镀铜将是较理想的铁基管件装饰电镀工艺。
[Abstract]:The key to decorative electroplating of iron-base pipe fittings lies in the selection of reasonable intermediate plating layer and reasonable electroplating process. For example, high cyanide Cu-Sn combined with full electroplating solution has low cost and good coating quality, but the solution is highly toxic, polished and polished with a large amount of labor. Bright nickel as the intermediate layer, the cost is very high; choose bright Ni-Fe alloy as the intermediate layer, electroplating solution maintenance is difficult; choose acid bright copper plating, then thin nickel as the intermediate coating, low cost, good effect. Electroplating of soft iron and chemical leaching of copper can prevent the replacement of copper powder and divalent iron pollution solution. Non-toxic alkaline bright copper plating instead of acid bright copper plating will be an ideal decorative plating process for iron-based pipe fittings.
【作者单位】： 哈尔滨风华机器厂

【相似文献】

相关期刊论文 前10条

1 于维新，，程军梅;电镀工艺及其发展方向[J];航天工艺;1995年02期

2 ;以石油为原料发酵法生产柠檬酸[J];今日科技;1975年10期

3 朱明高;;国内外电镀概况[J];今日科技;1978年05期

4 梁时骏;;问题解答[J];电镀与精饰;1983年06期

5 ;上海试剂附刊[J];化学世界;1983年09期

6 徐品;;植酸用于水处理[J];贵州环保科技;1989年02期

7 ;三乙醇胺无毒电镀铜锡合金工艺[J];今日科技;1970年09期

8 ;顺丁烯二酸羟基化合成酒石酸[J];上海化工;1973年04期

9 徐海;;改革工艺 化毒为利——武义县五金文具厂改有毒电镀为无毒电镀[J];今日科技;1980年03期

10 徐荣章,丁志金;利用山核桃、油桐、油茶蒲壳粗制碱合成焦磷酸钾[J];浙江林业科技;1982年03期

相关重要报纸文章 前1条

1 新华社记者 周亮　傅琰 赵东辉;珠三角企业家的新眼光[N];人民日报海外版;2008年

本文编号：1623446